Electrode has excellent welding properties, good slag removal and minimum spatter.

 

Product Name	Low Alloy Steel Electrode
Product No.	MHAE411-WE029
Standard
GB	AWS		JIS			DIN
E5010-A1	E7010-A1
Type of Covering
Welding Position			VD,F,  OH,H
Chemical Composition of Deposited Metal (%)
Chemical Composition	C	Mn	Si	S	P	Cr	Ni	Mo	V	Cu
Guarantee	≤0.12 0.074	≤0.60 0.33	≤0.40 0.11	≤0.03 0.010	≤0.03 0.009	—	—	0.40-0.65 0.48	—	—
Mechanical Properties of Deposited Metal
Test Item	Tensile Strengh Rm (MPa)	Yield point ReL (MPa)		Elongation  A4 (%)		Akv1(J)
Guarantee	≥490 580	≥390 470		≥22 24		—                 -20°C  70
Reference Current (DC+)
Electrode Diameter(mm)	2.5			3.2		4.0		5.0
Length(mm)	300			350		350		350
Welding Current(A)	50-70			80-120		110-150		140-200
Instructions
1.The electrode extremely easy absorption of moisture, should pay attention to the storage
2.When the packing is not good or is affected with damp,the electrodes must be baked under 70°C~80°C  for half an hour to an hour.
3.When welding 5.0mm elctrodes,adopt big thrust, small current as far as possible to improve welding performance.
Application
It is suitable for root passes, hot passes, filler and cover passes welding as well as for capping welding.