Super quality with low price,which has stable arc, fewer spatters, good slag detachability and excellent welding performance.

 

Product Name	Corrosion Resisting Low Alloy Steel Electrode
Product No.	MHAE411-WE024
Standard
GB	AWS		JIS			DIN
E5516-G	E8016-G
Type of Covering			Low hydrogen Potassium
Welding Position			F,V,   OH,H
Chemical Composition of Deposited Metal (%)
Chemical Composition	C	Mn	Si	S	P	Cr	Ni	Mo	V	Cu
Guarantee	0.05-0.12 0.065	≤0.90 0.60	≤0.60 0.30	≤0.03 0.007	≤0.03 0.011	0.40-0.65 0.44	—	0.40-0.65 0.49	—	—
Mechanical Properties of Deposited Metal
Test Item	Tensile Strengh Rm (MPa)	Yield point ReL (MPa)		Elongation  A4 (%)		Akv1(J)
Guarantee	≥550 620	≥460 485		≥19 25		—                -20°C 90
Reference Current (AC or DC)
Electrode Diameter(mm)	3.2			4.0				5.0
Welding Current(A)	90-120			140-180				170-210
Instructions
1.The Electrodes must be baked under 300~350  for an hour before Welding and used as soon as baking is completed.
2.The stains on the weldments, such as rust, oil stains, moisture, etc., must be cleared away before Welding.
3.When Welding, short arc must be used and stringer bead is suitable.
Application
Sutable for welding structures of skyscrapers and jumbo public buildings which fabricated by fire resisting and atmospheric corrosion and infection resistance steels.