Electrode has excellent welding properties, good slag removal and minimum spatter.

 

Product Name	Low Alloy Steel Electrode
Product No.	MHAE411-WE033
Standard
GB	AWS		JIS			DIN
E5515-G	E8015-G		D5316			EY5066NiMoBH5
Type of Covering			Low hydrogen sodium
Welding Position			F,V,   OH,H
Chemical Composition of Deposited Metal (%)
Chemical Composition	C	Mn	Si	S	P	Cr	Ni	Mo	V	Cu
Guarantee	— 0.075	≥1.00 1.25	≥0.80 0.50	≤0.03 0.012	≤0.03 0.018	≥0.30 0.005	≥0.50 0.003	≥0.20 0.003	≥0.10 0.010	≥0.20 0.016
Mechanical Properties of Deposited Metal
Test Item	Tensile Strengh Rm (MPa)	Yield point ReL (MPa)		Elongation  A4 (%)		Akv1(J)
Guarantee	≥550 590	≥460 480		≥19 24		—                -40°C  100
Reference Current (DC)
Electrode Diameter(mm)	2.5			3.2		4.0		5.0
Welding Current(A)	60-90			80-110		130-170		160-200
Instructions
1.The Electrodes must be baked under 300~350  for an hour before Welding and used as soon as baking is completed.
2.The stains on the weldments, such as rust, oil stains, moisture, etc., must be cleared away before Welding.
3.When Welding, short arc must be used and stringer bead is suitable.
Application
Welding medium carbon steel structures and low alloy steel structures.