Electrode has excellent welding properties, good slag removal and minimum spatter.

 

Product Name	Low Alloy Steel Electrode
Product No.	MHAE411-WE034
Standard
GB	AWS		JIS			DIN
E5518-C3	E8018-C3
Type of Covering			Iron powder low hydrogen sodium
Welding Position			VD,F,  OH,H
Chemical Composition of Deposited Metal (%)
Chemical Composition	C	Mn	Si	S	P	Cr	Ni	Mo	V	Cu
Guarantee	≤0.12 0.069	0.40-1.25 1.05	≤0.80 0.63	≤0.03 0.010	≤0.03 0.015	≤0.15 0.029	0.80-1.10 0.96	≤0.35 0.22	≤0.05 0.010	—
Mechanical Properties of Deposited Metal
Test Item	Tensile Strengh Rm (MPa)	Yield point ReL (MPa)		Elongation  A4 (%)		Akv1(J)
Guarantee	≥550 630	470-550 520		≥24 26		-40°C  ≥27    95
Reference Current (AC≥70V or DC)
Electrode Diameter(mm)	2.5			3.2		4.0		5.0
Welding Current(A)	70-110			100-140		140-180		190-240
Instructions
1.The Electrodes must be baked under 350  for an hour to two hours before Welding and used as soon as baking is completed.
2.The stains on the weldments, such as rust, oil stains, moisture, etc., must be cleared away before Welding.
3.When Welding, short arc must be used and stringer bead is suitable.
Application
Suitable for welding structures made by same grade low alloy steels, such as 15MnTi,15MnV, etc.