Electrode has excellent welding properties, good slag removal and minimum spatter.The weld metal is very resistant to hot crack.
Product Name | Corrosion Resisting Low Alloy Steel Electrode | |||||||||
Product No. | MHAE411-WE027 | |||||||||
Standard | ||||||||||
GB | AWS | JIS | DIN | |||||||
E6016-D1 | E9016-G | D5816 | E55548XXH5 | |||||||
Type of Covering | Low hydrogen Potassium | |||||||||
Welding Position | F,V, OH,H | |||||||||
Chemical Composition of Deposited Metal (%) | ||||||||||
Chemical Composition | C | Mn | Si | S | P | Cr | Ni | Mo | V | Cu |
Guarantee |
__ 0.063 |
≥1.00 1.47 |
≥0.80 0.30 |
≤0.03 0.015 |
≤0.03 0.014 |
≥0.30 0.59 |
≥0.50 0.72 |
≥0.20 0.22 |
≥0.10 0.12 |
≥0.20 0.31 |
Mechanical Properties of Deposited Metal | ||||||||||
Test Item |
Tensile Strengh Rm (MPa) |
Yield point ReL (MPa) |
Elongation A4 (%) |
Akv1(J) | ||||||
Guarantee |
≥620 650 |
≥530 550 |
≥17 23 |
— -40°C 80 | ||||||
Reference Current (AC or DC) | ||||||||||
Instructions | ||||||||||
1.The Electrodes must be baked under 350~380 for an hour before Welding and used as soon as baking is completed. | ||||||||||
2.The stains on the weldments, such as rust, oil stains, moisture, etc., must be cleared away before Welding. | ||||||||||
3.When Welding, short arc must be used and stringer bead is suitable. | ||||||||||
Application | ||||||||||
Suitable for welding structures fabricated by atmospheric corrosion & infection resisting alloy steels, e.g. Q500NQR1. |