Electrode has excellent welding properties, good slag removal and minimum spatter.The weld metal is very resistant to hot crack.

 

Product Name	Corrosion Resisting Low Alloy Steel Electrode
Product No.	MHAE411-WE028
Standard
GB	AWS		JIS			DIN
E7015-D2	E10015-G		D7016			EY624BXXH5
Type of Covering			Low hydrogen Sodium
Welding Position			F,V,   OH,H
Chemical Composition of Deposited Metal (%)
Chemical Composition	C	Mn	Si	S	P	Cr	Ni	Mo	V	Cu
Guarantee	__   0.042	≥1.00 1.49	≥0.80 0.30	≤0.03  0.007	≤0.03  0.012	≥0.30 1.05	≥0.50 1.25	≥0.20 0.22	≥0.10 0.13	≥0.20 0.13
Mechanical Properties of Deposited Metal
Test Item	Tensile Strengh Rm (MPa)	Yield point ReL (MPa)		Elongation  A4 (%)		Akv1(J)
Guarantee	≥690  730	≥600    640		≥16   19		__ -40°C  105
Reference Current (DC)
Electrode Diameter(mm)	2.0	2.5		3.2		4.0		4.0		5.8
Welding Current(A)	40-70	60-90		80-110		130-170		160-220		210-260
Instructions
1.The Electrodes must be baked under 300~350  for an hour before Welding and used as soon as baking is completed.
2.The stains on the weldments, such as rust, oil stains, moisture, etc., must be cleared away before Welding.
3.When Welding, short arc must be used and stringer bead is suitable.
Application
Suitable for welding important structures made by atmospheric corrosion and marine water corrosion low alloy steels,  e.g. WNQ690.