Electrode has excellent welding properties, good slag removal and minimum spatter.

 

Product Name	Low Alloy Steel Electrode
Product No.	MHAE411-WE037
Standard
GB	AWS		JIS			DIN
E8515-G	E12015-G					EY7953BXXH15
Type of Covering			low hydrogen sodium
Welding Position			F,V,   OH,H
Chemical Composition of Deposited Metal (%)
Chemical Composition	C	Mn	Si	S	P	Cr	Ni	Mo	V	Cu
Guarantee	— 0.065	≥1.00 1.80	≥0.80 0.35	≤0.03 0.009	≤0.03 0.016	≥0.30 0.004	≥0.50 0.010	≥0.20 0.70	≥0.10 0.009	≥0.20 0.007
Mechanical Properties of Deposited Metal
Test Item	Tensile Strengh Rm (MPa)	Yield point ReL (MPa)		Elongation  A4 (%)		Akv1(J)
Guarantee	≥830 900	≥740 800		≥14 19		—                 25°C   80
Reference Current (DC)
Electrode Diameter(mm)	2.0		2.5		3.2		4.0		5.0
Welding Current(A)	40-70		60-90		80-110		130-170		160-200
Instructions
1.The Electrodes must be baked under 380~400°C  for an hour to two hours before Welding and used as soon as baking is completed.
2.The stains on the weldments, such as rust, oil stains, moisture, etc. must be cleared away before Welding.
3.Welding can be appropriately bigger when rigidity preheated to 300, weld after 600 ~ 650 tempering, eliminate stress
Application
For welding important structures made by 830MPa grade of tensile strength or more low alloy steels.