superior quality electrode with low prices,with high penetration,negligible spatter and are very easy in dislogging.

 

Product Name	Low Alloy Steel Electrode
Product No.	MHAE411-WE045
Standard
GB	AWS		JIS			DIN
E5515-B2	E8018-B2
Type of Covering			Iron powder Low hydrogen Potassium
Welding Position			F,V,   OH,H
Chemical Composition of Deposited Metal (%)
Chemical Composition	C	Mn	Si	S	P	Cr	Ni	Mo	V	Cu
Guarantee	0.05-0.12 0.080	≤0.90 0.73	≤0.80 0.24	≤0.03 0.009	≤0.03 0.013	1.00-1.50 1.31	—	0.40-0.65 0.50	—	—
Mechanical Properties of Deposited Metal
Test Item	Tensile Strengh Rm (MPa)	Yield point ReL (MPa)		Elongation  A4 (%)		Akv1(J)
Guarantee	≥520 580	≥390 480		≥19 25		—                  25°C  180
Reference Current (AC≥70V or DC)
Electrode Diameter(mm)	2.0		2.5		3.2		4.0		5.0
Welding Current(A)	40-70		60-90		80-110		130-170		160-200
Instructions
1.The Electrodes must be baked under 350°C~380°C for an hour before Welding and used as soon as baking is completed.
2.The stains on the weldments, such as rust, oil stains, moisture, etc., must be cleared away before Welding.
3.When Welding, short arc must be used and stringer bead is suitable.
Application
Suitable for welding important structures made by 15CrMo steel, which work temperature below 520°C, such as boiler pipes, high pressure vessels, petroleum thermal cracking equirment, etc. Also it could weld cast steel of 30CrMnSi.