Specifications:
Grade: 5000 Series
Type: Plate
Tread plate 5 bar
Size:2.50*1200*2400mm
Weight: About 19.44kg/pc
Application: Aircraft fittings, camera lens mounts, couplings, marines fittings ect
Aluminum /Aluminium tread plate
1). Alloy: 1060, 3003, 5052 ,6061,6063
2). Temper: H22, H24, H26 ,T4,T6.
3). Pattern: 5bars, and diamond bars
4). Thickness: 0.3-6.0mm
5). Width: Under 1500mm
6). Length: Under 6500mm
Applications: You can use aluminum checkered plate in the floor of automobile, airplane, light rail, vehicle steps, stair treads, elevators, etc. You also can use checkered plate in your garage or workshop for a variety of purposes.
Grade: 5000 Series
Type: Plate
Tread plate 5 bar
Size:2.50*1200*2400mm
Weight: About 19.44kg/pc
Application: Aircraft fittings, camera lens mounts, couplings, marines fittings ect
Aluminium Tread plate 5 Bar:
Alloy: 1050, 1100, 3003, 5052
Temper: O, H14, H16, H18, H24, H26, H32, H34
Thickness: 0.15~4.0mm
Width: 400~1500mm
Length: 2000--6000mm
Alloy: 1050, 1100, 3003, 5052
Temper: O, H14, H16, H18, H24, H26, H32, H34
Thickness: 0.15~4.0mm
Width: 400~1500mm
Length: 2000--6000mm
5052/5021 aluminium tread plate has good workability, very good corrosion resistance, high fatigue strength, weldability, and moderate strength. This leads to its use in aircraft fuel/oil lines, fuel tanks, other transportation areas, sheet metal work, appliances and lighting, wire, and rivets.
Alloy nickname: UNS A95052; ISO AlMg2.5; Aluminium 5052-O; AA5052-O
Model Number: 5052
Description: Model Number: 5052
Aluminum /Aluminium tread plate
1). Alloy: 1060, 3003, 5052 ,6061,6063
2). Temper: H22, H24, H26 ,T4,T6.
3). Pattern: 5bars, and diamond bars
4). Thickness: 0.3-6.0mm
5). Width: Under 1500mm
6). Length: Under 6500mm
Applications: You can use aluminum checkered plate in the floor of automobile, airplane, light rail, vehicle steps, stair treads, elevators, etc. You also can use checkered plate in your garage or workshop for a variety of purposes.
5251/5052 0 5-BAR tread plate Properties
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 0.00000499ohm-cm | 0.00000499ohm-cm | AA; Typical |
| @Temperature 20.0 °C | @Temperature 68.0 °F | ||
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 22.1µm/m-°C | 12.3µin/in-°F | |
| @Temperature -50.0 - 20.0 °C | @Temperature -58.0 - 68.0 °F | ||
| 23.8µm/m-°C | 13.2µin/in-°F | AA; Typical; average over range | |
| @Temperature 20.0 - 100 °C | @Temperature 68.0 - 212 °F | ||
| 23.8µm/m-°C | 13.2µin/in-°F | ||
| @Temperature 20.0 - 100 °C | @Temperature 68.0 - 212 °F | ||
| 24.8µm/m-°C | 13.8µin/in-°F | ||
| @Temperature 20.0 - 200 °C | @Temperature 68.0 - 392 °F | ||
| 25.7µm/m-°C | 14.3µin/in-°F | ||
| @Temperature 20.0 - 300 °C | @Temperature 68.0 - 572 °F | ||
| 25.7µm/m-°C | 14.3µin/in-°F | average | |
| @Temperature 20.0 - 300 °C | @Temperature 68.0 - 572 °F | ||
| Specific Heat Capacity | 0.880J/g-°C | 0.210BTU/lb-°F | Estimated from trends in similar Al alloys. |
| Thermal Conductivity | 138W/m-K | 960BTU-in/hr-ft²-°F | AA; Typical at 77°F |
| Melting Point | 607.2- 649 °C | 1125- 1200 °F | AA; Typical range based on typical composition for wrought products 1/4 inch thickness or greater |
| Solidus | 607.2°C | 1125°F | AA; Typical |
| Liquidus | 649°C | 1200°F | AA; Typical |
| Processing Properties | Metric | English | Comments |
| Annealing Temperature | 343°C | 650°F | holding at temperature not required |
| Hot-Working Temperature | 260- 510 °C | 500- 950 °F | |
| Component Elements Properties | Metric | English | Comments |
| Aluminum, Al | 95.7 - 97.7 % | 95.7 - 97.7 % | As remainder |
| Chromium, Cr | 0.15 - 0.35 % | 0.15 - 0.35 % | |
| Copper, Cu | <= 0.10 % | <= 0.10 % | |
| Iron, Fe | <= 0.40 % | <= 0.40 % | |
| Magnesium, Mg | 2.20 - 2.80 % | 2.20 - 2.80 % | |
| Manganese, Mn | <= 0.10 % | <= 0.10 % | |
| Other, each | <= 0.050 % | <= 0.050 % | |
| Other, total | <= 0.15 % | <= 0.15 % | |
| Silicon, Si | <= 0.25 % | <= 0.25 % | |
| Zinc, Zn | <= 0.10 % | <= 0.10 % | |