PEI + GF30
Quick Details
|
Place of Origin:Guangdong China (Mainland)
|
Brand Name:HEYUE
|
Model Number:HY030
|
|
flame retardant:according to customers' requir...
|
filled with glass fiber:according to customers...
|
color:match any colors
|
Packaging & Delivery
|
Packaging Detail:
|
25kg/bag
|
|
Delivery Detail:
|
7-15 days after your order
|
Specifications
1. filled with 30% glass fiber;
2. flame retardant UL94-V0
3. resist the temperature to 340C
2. flame retardant UL94-V0
3. resist the temperature to 340C
Our PEI+30%GF with UL94-V0 have good performances on properties and can be replace Sabic 2300,2300R,2310,2310F,2310R. It can be widely used to produce air heater parts, automotive accessories, aircraft parts, medical parts etc.
HEYUE Standard PEI+30%GF with UL94-V0(our grade is 150G6) Specification:
|
High Performance Polyetherimide Materials
|
||||
|
PEI HY-030
|
||||
|
Properties
|
Standard
|
Condition
|
Unit
|
Value
|
|
Physical Properties
|
|
|
|
|
|
Specific Gravity
|
ASTM D792
|
23°C
|
g/cm3
|
1,53
|
|
Mold Shrinkage,Flow
|
ASTM D955
|
Cold mold, 48 hrs
|
%
|
0,2
|
|
Mold Shrinkage,Cross-Flow
|
Cold mold, 48 hrs
|
%
|
0,3
|
|
|
Moisture Absorption
|
ASTM D570
|
23 °C; 50 % RH
|
%
|
0,1
|
|
Filler Content, Glass Fiber
|
|
800°C/2h
|
%
|
30
|
|
Mechanical Properties
|
|
|
|
|
|
Tensile Strength
|
ASTM D638
|
50mm/min
|
Mpa
|
150
|
|
Elongation at Break
|
ASTM D638
|
50mm/min
|
%
|
2
|
|
Flexural Strength
|
ASTM D790
|
3mm/min
|
Mpa
|
220
|
|
Flexural Modulus
|
ASTM D790
|
3mm/min
|
Mpa
|
9000
|
|
Izod Impact, Notched
|
ASTM D256
|
|
J/m
|
80
|
|
Thermal Properties
|
|
|
|
|
|
Melting Point
|
DSC
|
23°C
|
°C
|
340
|
|
CTE
|
ASTM D696
|
-20~150°C
|
µm/m°C
|
55,8
|
|
HDT
|
ASTM D648
|
1.8 Mpa
|
°C
|
210
|
|
Flammability
|
UL94
|
1.6 mm
|
|
V0
|
|
Electrical Properties
|
|
|
|
|
|
Dielectric Constant
|
IEC 60250
|
1 MHz
|
|
3,1
|
|
Dielectric Strength
|
IEC 60243
|
S/T, in oil
|
kV/mm
|
28
|
|
Dissipation Factor
|
IEC 60250
|
1 MHz
|
|
0,015
|
|
Volume Resistivity
|
IEC 60093
|
23°C
|
ohm·cm
|
>1015
|
|
Materials Drying Process
|
|
|||
|
Drying Temperature
|
140~150°C
|
|||
|
Drying Time
|
4~6 h
|
|||
|
Maximum Moisture Content
|
0,02%
|
|||
|
Injection Process
|
|
|||
|
Mold Temperature
|
120~150°C
|
|||
|
Front Cylinder Temperature
|
310~370°C
|
|||
|
Middle Cylinder Temperature
|
318~375°C
|
|||
|
Behind Cylinder Temperature
|
315~370°C
|
|||
|
Nozzle Temperature
|
310~380°C
|
|||
|
Melt Temperature
|
310~370°C
|
|||
|
Injection pressure
|
82~125Mpa
|
|||
|
Back Pressure
|
0.3~0.5Mpa
|
|||
|
Screw speed
|
40~80 rpm
|
|||
|
The data is just value of experiments, and can't be used as acceptance standards.
|
||||