PBAT modified resin /PLA modified resin is a kind of ivory granular hemi crystalline solid. It is tasteless, and insoluble in water, but soluble in THF, chloroform. It can be biodegradable in Compost conditions.

Tensile strength(Mpa)≥10Mpa (Longitudinal / horizontal) GB/T 1040-1992

Elongation at break (%) ≥304/280%(Longitudinal / horizontal) GB/T 1040-1992

Right Angle tear strength(KN/n) ≥80 (Longitudinal / horizontal) GB/T 1130-1991

Sealing strength (m＜6kg) 6.2 GB/T 21661-2008

Water leakage Not leak GB/T 21661-2008

Mention crane test without damage GB/T 21661-2008

Relative density 1.20±0.05 GB/T1033-1986

Melting point℃120-140 GB/T 19466.3-2004

Molten index, g/10min,190℃ 2-10 GB/T 3682-2000

Tensile strength(Mpa)≥18/ 11Mpa (Longitudinal / horizontal) GB/T 1040-1992

Elongation at break (%) ≥260/ 245%(Longitudinal / horizontal) GB/T 1040-1992

Right Angle tear strength(KN/n) ≥85 (Longitudinal / horizontal) GB/T 1130-1991

Sealing strength (m＜9kg) 7.2 GB/T 21661-2008

Water leakage Not leak, GB/T 21661-2008

Mention crane test without damage GB/T 21661-2008

Relative density 1.25±0.05 GB/T1033-1986

Melting point℃≥150 GB/T 19466.3-2004

Molten index, g/10min,190℃ 2-10 GB/T 3682-2000

Glass transition temperature of the℃50-60℃GB/T 19466.2-2004

 

Packaging: 25KG paper-plastic bag /According to customers.