Product: AISI O-1,DIN 1.2510

 

Key words: oil hardening die steel,tool steel,die steel,specialty steel,steel bar,hotwork,coldwork,forged bar,alloy tool steel,flat bar, round bar

 

Typical Analysis:

C: 0.85-1.00

Si:0.10-0.50

Mn:1.00-1.40

P: MAX 0.030

S: MAX 0.030

Cr:0.40-0.60

V: MAX 0.30

W: 0.40-0.60

 

Similar Grades: DIN 1.2510,GB/T 9CrWMn+v

 

Advantages:

1.Moderately wear resistant.

2.Hardens from low temperature.

3.Easy to machine.

 

Availability:

Flat,round,normal forging sizes.

 

Machinability:

In the annealed condition O-1 carries a rating of 90% of a 1% carbon tool steel. It also has a high grindability rating.

 

Annealing:

Preferably O-1 should be atmosphere or vacuum annealed at 1425°F. About two or three hours at temperature is required. Then the charge should be furnace cooled 100° per hour and then cooled in still aie from 1000°F. Annealed hardness is 187 to 217 Brinell.