Cr26 White Iron Shell Liners For Ball Mill Liners With More Than HRC56 Hardness And 10J AK
1.Material: Cr26 white iron.
2.Hardness:More than HRC56;
3.AK≥10J;
4.The materials conform to GB/T 8263-2010.
1. We select Cr26 white iron as the material of shell liners for longer service life in the application.
2.Hardness:More than HRC56;
3.AK≥10J;
4.The materials:
BS 4844 3E,
AS 2027 CrMo 15/3,
AS 2027 CrMo 20/2/1,
AS 2027 Cr27,
ASTM A532 Class III type A 25% Cr,
ASTM A532Class II type B 15% Cr-Mo.
Application :ball mills
Material :high chrome white iron
Dimensions :As per drawings
Hardness :More than HRC56
Chemical Composition :Every furnace heat shall be analysed by Spectrometer
Dimensional Checking & Gauging :100% check 100%
Casting Soundness :Level 2 of AS2574 or equivalent standard
Surface Finish :Visual inspection after shot blasting
Reporting :Providing process, inspection & test result data