Cement lime fly ash style aerated block raw material proportion

name	unit	Cement lime fly ash
flash	%	65-70
cement	%	6-15
lime	%	18-25
gypsum	%	3-5
Aluminum powder paste(600kg/m3)	1/10000	8
Water & material rate		0.60-0.65
Casting system	OC	36-40
Aluminum mixing time	S	30-40

Cement lime fly ash autoclaved aerated concrete block production line Capacity: from 50000 cubic meter to 300,000 cubic meters per year.
Cement lime fly ash autoclaved aerated concrete block production line Equipments: stocking raw materials, mixing, molding, forming, cutting, evaporating and curing, crane cramp, transporting etc.,
1 Product weight is according to 600kg/m3 to control.
2 annual capacity 300,000M3.
3 set raw material proportion: cement 6.5%, raw lime 23%, flyash 68%, gypsum 3%, aluminum paste powder 350g/M3.
4 water and material rate 0.631
5 one mould product 2.88M3
6 Casting slurry cycle time 5-6 minutes, cut cycle time 5 minutes.
7 casting slurry temperature 38-42 degree
8 body quiet stop. Time is 1.5-2.5hours, temperature 50-90 degree, after quiet stop body strength is 0.15-0.18Mpa
9 Steam curing cycle time, come in and out autoclave about 0.5hour, steam curing cycle time about is 6 hours/1.6Mpa, total 6.5 hours.