Specifications
High strength liquid silicone rubber for trademark
SB4140 is room temperature addition-cured liquid molding silicone rubber with low viscosity, which has all kinds of the advantages and features of addition cured silicone.
High strength liquid silicone rubber for trademark Application:
It can be used for making labels separately, and also can be fabricated into trademarks thorough cloth pressing and leather pressing . Generally , it is applied to the trademarks of jeans, shoes, toy, ect.
High strength liquid silicone rubber for trademark features:
1, Non pollution environment, environment friendly silicone ink,
2, Non harm to human body. Caused by the organic solvent into environment friendly, in noxious ink
3, None cause environmental problems when test and destroy ester of silicone ink.
4, Silicon Ink with SGS approval, the silicone ink based on safety design easily pass any international inspection
5, Cured silicone in with high elastic, soft smooth hand feeling when touch, slippery, high stretchable and non bleeding
6, adhered on textile fiber well after being cured and forms elastomeric of silicone.
7, Good ink for silicone rubber products and latex with great adhesive.
8, Produce high tear strength, create high quality printing effect
9, Moderate fluidity and cure time application. Easy process
10, Low and higher temperature resistance (-50 to 300)
11, Special silicone elastomeric recovery capacity, flexibility, velvet, resistance to oil, solvent, and other etc,
12, no harm to human body caused by the organic solvent into environment friendly, in noxious ink
high strength liquid silicone rubber for trademark Datasheet:
|
Model
|
SB4130
|
SB4140
|
|
Appearance
|
Transparent
|
Tranparent
|
|
Hardness(shore A)
|
30± 2
|
40± 2
|
|
Mix ratio(A: B)
|
01:01
|
01:01
|
|
Viscosity(mPa. S)
|
65000± 2000
|
67000± 2000
|
|
Tensile strength(Mpa)
|
4.2
|
4.1
|
|
Tear-strength(KN/m)
|
17± 2
|
17± 2
|
|
Elongation(%)
|
275
|
270
|
|
Pot life/working time(25)
|
6-24hrs
|
6-24hrs
|
|
curing time(100-120)
|
3-10(minutes)
|
3-10(minutes)
|