Standard: YS/T 310-2008
Main Application:
Hot-Galvanizing Alloy is used mainly within Steel Galvanizing industry．
Specification and Packaging:
1000±100kg, 1870±120kg per ingot． The measurements are 1180×590×280mm 1700×550×400mm according to buyer's option.
Physical and chemical properties
It is with high proportion and able to be casted into different shape of parts which are exac—titude and surface cleaned．The surface can be treated with the art of electroplate, spray-wiped and spray—paint．it's and when in contacts with vapor(eIectaolyte), chemical enoding of caystal will tahe place．While it is melting or casting, it will not become magnet, causticity and glutinosity．It have good mechanical performance and grind—resistance in the normaI temperature．
Transportation, storage
It is not permitted to package or transport Hot—GaLvanizing Alloy ingots with acid, alkaline, salt or any other type of corrosive material．The ingots should be stored in a dry, ventilated and non—corrosive environment, top revent wet．
Main Application:
Hot-Galvanizing Alloy is used mainly within Steel Galvanizing industry．
Specification and Packaging:
1000±100kg, 1870±120kg per ingot． The measurements are 1180×590×280mm 1700×550×400mm according to buyer's option.
Physical and chemical properties
It is with high proportion and able to be casted into different shape of parts which are exac—titude and surface cleaned．The surface can be treated with the art of electroplate, spray-wiped and spray—paint．it's and when in contacts with vapor(eIectaolyte), chemical enoding of caystal will tahe place．While it is melting or casting, it will not become magnet, causticity and glutinosity．It have good mechanical performance and grind—resistance in the normaI temperature．
Transportation, storage
It is not permitted to package or transport Hot—GaLvanizing Alloy ingots with acid, alkaline, salt or any other type of corrosive material．The ingots should be stored in a dry, ventilated and non—corrosive environment, top revent wet．