Forged Grinding Steel Ball

1.Feature:

1) In general, forged steel ball has high hardness: surface hardness to 55-68 HRC, volume hardness of 50-63 HRC

2) impact toughness high: impact toughness more than 12 J / cm2.

3) broken rate is low: the actual broken rate is not higher than 1%.

4) loss of grinding forged steel ball round rate is low.

 

2.Forged Grinding Ball

Chemical composition and Hardness:

(1)Alloy Grinding Steel Ball

Hardness: HRC45-55

Chemical Elements:

C:0.37-0.55 Si:0.17-0.37 Mn:0.50-0.80 S:≤0.40 P:≤0.40 Cr:≤0.25 Ni:≤0.25

(2)Forged Manganese Alloy Grinding Steel ball

Hardness: HRC50-60

Chemical Elements:

C:0.42-0.70 Si:0.17-0.37 Mn:0.70-1.00 S:≤0.40 P:≤0.40 Cr:≤0.25 Ni:≤0.25

(3)Forged High Efficiency Grinding Steel Ball

Hardness: HRC55-67

Chemical Elements:

C:0.70-0.85 Si:0.17-0.37 Mn:0.70-1.20 S:≤0.35 P:≤0.35 Cr:0.2-1.0

 

3.Casting Grinding Ball

Size: Diameter 17-150mm

Description:

High Hardness, Good Wear Resistance, Good Toughness, Even wearing, No Breakage

Product Category:

(1)Low Chromium Casting Grinding Steel Ball

Hardness: HRC45-55

Chemical Elements:

C:2.2-2.5 Si:≤1.2 Mn:≤1.0 Cr:0.8-1.8 Mo: Minim Cu: Minim S:≤0.15 P:≤0.15

(2)Middle Chromium Casting Grinding Steel Ball

Hardness: HRC48-60

Chemical Elements:

C:2.2-3.3 Si:≤1.2 Mn:≤1.0 Cr:2.5-9.0 Mo: Minim Cu: Minim S:≤0.15 P:≤0.15

(3)High Chromium Casting Grinding Steel Ball

Hardness: HRC55-65

Chemical Elements:

C:1.6-3.3 Si:≤1.0 Mn:≤1.0 Cr:10-13 Mo:0.3-1.5 Cu:0.2-1 S:≤0.10 P:≤0.10

(4)Super High Chromium Casting Grinding Steel Ball

Hardness: HRC55-65

Chemical Elements:

C:2.0-3.3 Si:≤1.0 Mn:≤2.5 Cr:≥15 Mo:1.0-2.0 Cu:0.8-1.5 S:≤0.10 P:≤0.10

 

4.Main Process of Forged Steel Ball

(1)Raw material.(2)Cutting.(3)Heating.(4)Forging.(5)Quenching.(6)Tempering.(7)Testing.(8)Qualified Products.(9)Packing

 

5.Applied Field

1).Cement Plants 2).Mines 3).Power stations 4).Chemical Industries 5).Grinding Mill, Ball mill, Coal mill

 

6. Products Name

Grinding Ball,Grinding Media