transparent silicone rubber for shoe insole making description :
transparent silicone rubber for shoe insole making is generally named as two-part addition silicone rubber that vulcanises at room temperature.Part A is a flowable liquid, part B is the curing agent(platinum catalyst). It features an exceptional fluidity ,good operability,excellent physical properties and very low shrinkage. The mixing ratio between Part A and Part B can be 10:1 or 1:1.
transparent silicone rubber for shoe insole making main application:
- Rapid prototyping (urethane casting/silicone tooling/vacuum casting)
- Concrete moulding
- PU resin casting
- General Mouldmaking
- Superior manual mold designs
- Cake/Chocolate molds
transparent silicone rubber for shoe insole making main properties:
- almost nil shrinkage
- high chemical resistance to aggressive components of some types of resins
- good tear strength (this feature ensures higher resistance to wearing and shearing)
- high degree of precision in reproduction
- high dimensional stability over time and non-deformability
- high resistance to high temperatures and ageing (resit to -60-200°C)
- excellent non-stick effect
- environmental, odorless and nontoxic
transparent silicone rubber for shoe insole making
(The mixing ratio of part A and part B can be adjusted to 1:1or 10:1) (25°C)
|
Product
|
E-615
|
E-620
|
E-625
|
E-630
|
E-642
|
|
Appearance
|
Translucent
|
Translucent
|
Translucent
|
Translucent
|
Translucent
|
|
Hardness(shore A)
|
15±2
|
20±2
|
25±2
|
30±2
|
42±2
|
|
Mix ratio(A:B)
|
1:1
|
1:1
|
1:1
|
1:1
|
10:1
|
|
Viscocity Part A(mPa.s)
|
22000±2000
|
23000±2000
|
27000±2000
|
25000±2000
|
55000±2000
|
|
Viscocity Part B(mPa.s)
|
1900±500
|
1900±500
|
1800±500
|
2400±500
|
150±50
|
|
Tensile strength (MPa)
|
5.2
|
5.7
|
6.7
|
5.5
|
7.6
|
|
Tear-strength (kN/m)
|
25
|
26
|
23
|
24
|
22
|
|
Elongation(%)
|
569
|
581
|
480
|
410
|
450
|
|
Density
|
1.05
|
1.05
|
1.07
|
1.13
|
1.14
|
|
Pot life/working time (mins)
|
30-40
|
30-40
|
30-40
|
30-40
|
30-40
|
|
Curing time/setting time (hrs)
|
3-4hrs(25°C)
120-30mins(60°C)
|
3-4hrs(25°C)
120-30mins(60°C)
|
3-4hrs(25°C)
120-30mins(60°C)
|
3-4hrs(25°C)
20-30mins(60°C)
|
6-8hrs(25°C)
130-50mins(60°C)
|
|
Shrinkage rate (%)
|
0.1
|
0.1
|
0.1
|
0.1
|
0.1
|
Notice:
All above addition silicone is forbidden to mix with organic compounds of condensation cure silicone rubber,otherwise, the silicone rubber will not cure, and also should not mix with organic compounds containing S, P, N as well as metallic salt of organic acids. It also will cause this product cure uncompletely or not cure.
For more information, pls feel free to contact Christy.