Product Feature
RTV-2 Silicone is a newly insulating material silicon of silicon compounds.
It cures without heat, corrosion and just with little shrinkage. It can be applied to the sealing and pouring of various electronic components, and then forming insulation system.
Features:
RTV-2 Silicone is a newly insulating material silicon of silicon compounds.
It cures without heat, corrosion and just with little shrinkage. It can be applied to the sealing and pouring of various electronic components, and then forming insulation system.
Features:
Room temperature vulcanize, and easy to operate; l Maintain flexibility at a wide temperature range, and excellent insulation performance; l Waterproofing, moisture-proof, mouldproof, dustproof, and fixed components; l Resistance to Chemical dielectric, anti-yellowing, resistance to climate ageing.
Typical Application
Typical Application
HY-9300# silicone is suitable for bonded seal of electronic components, power module and control module, which requires waterproof and insulation. It can be broadly used for LED screen, Wind Power Generator, PCB substrate, etc.
Technical Parameters
| Before Curing | Appearence | Black/Transparent Fluid |
| Density(25°C g/ml) | 0.98±0.02 | |
| Viscosisty(25°Ccps) | Part A 500±100:Part B:800±100 | |
| Mixing Ratio | A:B=1:1(By weight) | |
| Operating Time(25°C hr) | 5 | |
| Curing time(80°C hr) | 0.5 | |
| After Curing | Hardness(Shore A) | 0-40 |
| Dielectric Strength(KV/mm) | >23 | |
| Volume Resistance(Ω.Cm) | 1.0×10 15 | |
| Permittivity(1.2MHz) | >3.0 | |
| Temperature Resistence(°C) | 60~200 | |
| Fire Resistance | UL94-V1 |
(Pls note: all data of this product above in 25 °C with 55% humidity conditions. We don’t guarantee a same data if testing under different conditions, or when data was regenerated)
TECHNICAL GUIDELINES 1, Pls put part A and part B in separate container and stir evenly before mixing the two part together. 2, Weight Ratio: part A: part B = 1:1 3, Deaeration the mixture under 0.08 MPa for 3 minutes. 4, The temperature influences the curing time of 9301. When in too low temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization
TECHNICAL GUIDELINES 1, Pls put part A and part B in separate container and stir evenly before mixing the two part together. 2, Weight Ratio: part A: part B = 1:1 3, Deaeration the mixture under 0.08 MPa for 3 minutes. 4, The temperature influences the curing time of 9301. When in too low temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization