pad printing silicone rubber with high printing times application:
Silicon rubber,pad printing silicone rubber with high printing times is mainly used for printing irregular patterns of plastic toys, electroplating products, electronic toys, trademarks. Silicon pad is a carrier which transfer printing the patterns on the steel plate onto the toy products' surface.
pad printing silicone rubber with high printing times features:
Pad printing silicon rubber with high print times and abrasion resistance, good printing effect, permanent and durable, all kinds of colors are available and our catalyst is free charged.
pad printing silicone rubber with high printing times operation instructions:
pad printing silicone rubber with high printing times is two-component silicone, part A is the liquid silicon rubber, part B is the catalyst. The usual mxing ratio for silicone rubber and catalyst is 100 : 2-3, eg. we take 100grams of liquid silicon rubber,then we add 2-3 grams catalyst, mix then evenly and pour it to your mold. Then after 2-4 hours, you will obtain a printing pad.
Admixture amount of curing agent and pad printing silicone rubber with high printing times reactions:
5.1Added with 1% of curing agent,silicon can still flow within 2.5 hours,mold can be released in 6-8 hours.
5.2Added with 2% of curing agent,silicon can still flow within 50 minutes to 1 hour,mold can be released in 2-3 hour
5.3Added with 3% of curing agent,silicon can still flow within 28-30 minutes,mold can be released in 1.5-2 hours.
5.4Added with 4% of curning agent,silicon can still flow within 10-15 minutes,mold can be released in 1-1.5 hours.
5.5 Curing agent reaction rate is related with weather and temperature. Under 25 degree,they can be added according to the instruction or at double amount in winter or under subzero temperature.
5.1Added with 1% of curing agent,silicon can still flow within 2.5 hours,mold can be released in 6-8 hours.
5.2Added with 2% of curing agent,silicon can still flow within 50 minutes to 1 hour,mold can be released in 2-3 hour
5.3Added with 3% of curing agent,silicon can still flow within 28-30 minutes,mold can be released in 1.5-2 hours.
5.4Added with 4% of curning agent,silicon can still flow within 10-15 minutes,mold can be released in 1-1.5 hours.
5.5 Curing agent reaction rate is related with weather and temperature. Under 25 degree,they can be added according to the instruction or at double amount in winter or under subzero temperature.
(Note: curing agent can not be added above the 4 maximum level and the normal proportion is
2%. If more than 4 is applied,the silicon will condensate too fast for normal usage).Above is the mixing data for silicon and curing agent,the precise result of hundreds of times of our experiments. Provided that you arrange production according to our instruction,you are sure to manufacture first class products and maximize your profitthis is not only the need of,but also our responsiblity for and a satisfactory answer to our customers.
Any more information, pls feel free to contact Christy at any time.
2%. If more than 4 is applied,the silicon will condensate too fast for normal usage).Above is the mixing data for silicon and curing agent,the precise result of hundreds of times of our experiments. Provided that you arrange production according to our instruction,you are sure to manufacture first class products and maximize your profitthis is not only the need of,but also our responsiblity for and a satisfactory answer to our customers.
Any more information, pls feel free to contact Christy at any time.