Property: Made of natural special grade magnesite, which is refined by floating, light burned, fine grinding, briquetting, sintered in shaft kiln at high temperature.
High purity, excellent bulk density, good raw material for bricks, unshaped refractories.
High purity, excellent bulk density, good raw material for bricks, unshaped refractories.
1. DBM97.5
MgO 97.5% min
SiO2 0.5% max
CaO 1.1% max
Fe2O3 0.6% max
LOI 0.2% max
B.D. 3.3g/cm3 min
Size 0-30mm
2. DBM97
MgO 97% min
SiO2 0.8% max
CaO 1.2% max
Fe2O3 0.9% max
LOI 0.3% max
B.D. 3.27g/cm3 min
Size 0-30mm
3. DBM96
MgO 96.5% min
SiO2 0.9% max
CaO 1.2% max
Fe2O3 1.0% max
LOI 0.3% max
B.D. 3.25g/cm3 min
Size 0-30mm
4. MZ-96
MgO 95.5%min
CaO 2%max
Apparent Porosity 18%max
Cold Crushing Strength 60%min
0.2MPA refractoriness under load 1650℃ min
5. MZ-97
MgO 96.5%min
CaO 1.5%max
Apparent Porosity 18%max
Cold Crushing Strength 60%min
0.2MPA refractoriness under load 1680℃ min
6. MZ-98
MgO 97.5%min
CaO 1.0%max
Apparent Porosity 18%max
Cold Crushing Strength 60%min
0.2MPA refractoriness under load 1700℃ min