Property: Made of high quality fused magnesite, high purity magnesite and high purity graphite, with high quality phenol resin as binding agent, by means of high pressure forming.
Strong high temperature intensity and oxidation resisting.
Strong high temperature intensity and oxidation resisting.
1. MC-10A
MgO 82%min
C 10%min
B.D. 3g/cm3 min
Apparent Prosity 3% max
Cold Crushing Strength 45MPA min
Hot Modulus of Rupture 10MPA min (1400℃X0.5h)
2. MC-10B
MgO 80%min
C 10%min
B.D. 2.95g/cm3 min
Apparent Prosity 4% max
Cold Crushing Strength 40MPA min
Hot Modulus of Rupture 8MPA min (1400℃X0.5h)
3. MC-10C
MgO 78%min
C 10%min
B.D. 2.90g/cm3 min
Apparent Prosity 4% max
Cold Crushing Strength 35MPA min (1400X0.5h)
4. MC-14A
MgO 78%min
C 14%min
B.D. 3g/cm3 min
Apparent Prosity 3% max
Cold Crushing Strength 45MPA min
Hot Modulus of Rupture 14MPA (1400℃X0.5h)
5. MC-14B
MgO 76%min
C 14%min
B.D. 2.95g/cm3 min
Apparent Prosity 4% max
Cold Crushing Strength 40MPA min
Hot Modulus of Rupture 10MPA min (1400℃X0.5h)
6. MC-14C
MgO 76%min
C 14%min
B.D. 2.90g/cm3 min
Apparent Prosity 4% max
Cold Crushing Strength 35MPA min
Hot Modulus of Rupture 8MPA min (1400℃X0.5h)
7. MC-18A
MgO 74%min
C 18%min
B.D. 3g/cm3 min
Apparent Prosity 3% max
Cold Crushing Strength 45MPA min
Hot Modulus of Rupture 12MPA min (1400X0.5h)
8. MC-18B
MgO 72%min
C 18%min
B.D. 2.95g/cm3 min
Apparent Prosity 4% max
Cold Crushing Strength 40MPA min
Hot Modulus of Rupture 10MPA min (1400℃X0.5h)
9. MC-18C
MgO 70%min
C 18%min
B.D. 2.90g/cm3 min
Apparent Prosity 4% max
Cold Crushing Strength 35MPA min
Hot Modulus of Rupture 8MPA min (1400℃X0.5h)