AUN---High Wear-resisting Heat Shrinkable Tubing
Applications
A special-purpose heat shrinkable tubing, made by modified polyolefin. It has high abrasion resistance property, especially suitable for protecting reciprocating motion applications.
Characteristics
High shrink ratio
High abrasion resistance property
Chemical resistance
Flexible
Operating temperature range
Operating temperature: -55°Cto125°C
Minimum shrink temperature :70℃
Minimum fully recovery temperature:110℃
Technical data
|
Project |
Test Method |
Typical data |
|
Operating temperature range |
IEC216 |
-55℃~100℃ |
|
Minimum shrinkage temperature |
----- |
120℃ |
|
Tensile strength |
ASTM D 2671 |
18MPa |
|
Tensile fracture rate |
ASTM D 2671 |
700% |
|
Density |
ISO R1183D |
0.94g/cm3 |
|
Dielectric strength |
IEC243 |
25KV/mm |
|
Volume resistivity |
IEC243 |
1015Ω.cm |
|
Permittivity |
IEC243 |
2.5 |
|
Longitudinal shrinkage |
ASTM D 2671 |
±5% |
|
Side wall |
ASTM D 2671 |
10% |
Product dimensions
|
Part Number |
Expanded(mm) |
Recovered(mm) |
Standard length [mm] |
||
|
Inside Diameter |
Nominal Thickness |
Max. inside Diameter |
Min. Thickness. At any point |
||
|
Ordinary type |
|||||
|
AUN-3C |
2.2±0.1 |
≥0.19 |
0.63 |
0.35±0.02 |
40 |
|
AUN-4C |
2.7±0.1 |
≥0.17 |
0.63 |
0.35±0.02 |
40 |
|
AUN-3R |
2.2±0.1 |
≥0.19 |
0.63 |
0.35±0.02 |
40 |
|
AUN-4R |
2.7±0.1 |
≥0.17 |
0.63 |
0.35±0.02 |
40 |
|
Thickening type |
|||||
|
AUN2-3C |
2.4±0.1 |
≥0.4 |
0.63 |
0.8±0.05 |
40 |
|
AUN2-3R |
2.2±0.1 |
≥0.4 |
0.63 |
0.7±0.05 |
40 |
|
150℃High-temperature wear-resistant wiping edge |
|||||
|
AUN-150 |
1.4±0.1 |
≥0.19 |
0.55 |
0.35±0.05 |
40 |