| Place of Origin: | China (Mainland) |
|---|---|
| Brand Name: | CL |
| Model Number: | CLTINI |
| surface: | polished surface |
| Marterial: | Gr1 Gr2 |
| Sandard: | ASTM B 163 |
| Method: | cold rolled |
| Condition: | annealed |
| Application: | 70% Ni was used in produce stainless steel and heat resistance steel |
Quick Details
Specifications
1. Material: Ni200, Ni201
2. Standard:ASTM B161, ASTM B163,GB/T2822-8
3. Size range: OD: 10-110mm
Wall thickness: 0.4-10mm
Max length15,000mm
4.Method: cold rolled
5.Condition: annealed
6.Application
1)70% Ni was used in produce stainless steel and heat resistance steel
2)15% of the Ni in the world was used as electroplating.
3)Used as catalyst in oil industry
4)Ni is one of the chemical source of energy ,the need material for battery
5)Used to make pigment,dye,ceramic,and ferrite.
7.Properties
|
|
Density |
Melting point |
Coefficient of expansion |
Modulus of rigidity |
Modulus of elasticity |
Electrical resistivity |
|
Ni200 |
8.9g/cm3 |
1446°C |
13.3 μm/m °C (20-100°C) |
81kN/mm2 |
204kN/mm2 |
9.6μW? cm |
|
Ni201 |
1446°C |
13.1μm/m °C(20-100°C) |
82kN/mm2 |
207kN/mm2 |
8.5μW? cm |
8.Chemical Composition
|
Grade |
Element Composition/% |
|||||||
|
Ni+Co |
Mn |
Cu |
Fe |
C |
Si |
Cr |
S |
|
|
Ni201 |
≥99.0 |
≤0.35 |
≤0.25 |
≤0.30 |
≤0.02 |
≤0.3 |
≤0.2 |
≤0.01 |
|
Ni200 |
≥99.0 |
/≤0.35 |
≤0.25 |
≤0.30 |
≤0.15 |
≤0.3 |
≤0.2 |
≤0.01 |