E6010-welding-rod,E6010 welding rods

· Description: 

AWS E6013 is a low-carbon steel electrode with a high titanium  Zander.welding.industry

Shandong zander resourcing company limited-zander welding industry

o coating and can be used on AC or DC

o It has excellent welding technological properties

o The arc is stable

o The spatter is small

o The slag viscosity is moderate

o It can be used freely

o The slag is easy to clean

o The welded seam is smooth and fine and easy to re-strike the arc

Applications: Zander.welding.industry

Shandong zander resourcing company limited-zander welding industry

o Used to weld low carbon structure and low alloy steel structure, such as 16Mn and more

o Before welding, it is necessary to clean the work piece and remove the impurities such as oil, grease rust and moisture, bake the electrode at the temperature of about 350°C for one hour

o Welding must be carried out under short arc and is suitable for narrow path

o When used DC, it must be connected with positive polarity

Zander.welding.industry

Shandong zander resourcing company limited-zander welding industry

· Chemical composition of wire: C Mn Si S P ≤0.12 0.3-0.6 ≤0.35 ≤0.035 ≤0.040%

· Mechanical properties of deposited metal: 

o Test item: σb(MPa) σc(MPa) δs(%) Akv(°C)(J)

o Guarantee value: ≥420 ≥330 ≥17

· Recommended welding current: 

o Electrode diameter: 2.0, 2.5, 3.2, 4.0, 5.0mm

o Current range: 40-70  50-80 80-120 150-190  180-240A

· Welding electrode e6013 feature:

· Stable arc, less splash, less smoke

· Easy for removal of slag layer

· Easy for striking arc and re-striking arc good appearance, suitable to work in all position

· Welding electrode productive technology:

1 Rods of four main alloys: 

o Cobalt-base alloy, nickel-base alloy and iron-base alloy and stellite alloy

2 Wear-resistant, corrosion-resistant, high temperature-resistant and shock-resistant

3 Process: OXY, TIG, plasma welding

·  Our product advantage:

Zander.welding.industry

Shandong zander resourcing company limited-zander welding industry

4 While welding operation,electrode manipulation is freely,hand felling is comfortable with little spatter and the welding slag is easy to flake (normally it flakes automatically while down hand welding and angle welding) the forming of welding seam is formed beautifully

5 The corrosion resistance of the weld metal is extremely good and its mechanical character and its crack resistance are fine

· Notes

6 Welding electrodes shall be 150°C baking 1 hour

7 Welding DC power supply as far as possible, because the AC welding penetrate.