Development Process:
This product was developed in June 2013 and filled the market domestic blanked . Choosing alumina and iron filings as raw material ,this products is sintered at high temperature in reducing atmosphere with homogenized and matching process. It contains no chrome and has good property of adhering coating. It can be widely used in kiln brick for sintering zone of rotary kiln such as sintering zone of cement rotary kiln.
Techinical Index:
Index Product | Chemical Composition (%) | |||||
AL2O3 | MgO | SiO2 | Fe2O3 | B.D(g/cm3) | Moisture Absorption(%) | |
FA-1.5 | 50-55 | 4-5 | ≤1.50 | 39-42 | ≥3.55 | ≤3.0% |
FA-0.6 | 50-55 | 4-5 | ≤0.60 | 39-44 | ≥3.55 | ≤2.0% |
Grain Size:
| Specifcation(mm) | Sieve Mesh | Typicl Value of Particle Composition(%) | min-max(%) |
| 5-3 | |||
+5mm |
| 4 | 0-8 |
+4mm | 5 | 40 |
|
+2.8mm | 7 | 34 |
|
-2.8mm | 7 | 5 | 0-8 |
3-1 | |||
+2.8mm | 7 | 4 | 0-8 |
+2.0mm | 10 | 40 |
|
+1.0mm | 18 | 30 |
|
-1.0mm | 18 | 5 | 0-10 |
1-0 | |||
+1.0mm | 18 | 3 | 0-8 |
+0.5mm | 35 | 40 |
|
+0.125mm | 120 | 25 |
|
-0.125mm | 120 | 20 | 10-30 |
1.Wide sizes variety available against customers' request
2.Mesh analysis according to GB/T6003.1-1997(ISO3310.1-1997)or tailor-made processing agreement
3.Package:25kg,1000kg or on customers' request.