Product Main

Quick Details

Place of Origin: China (Mainland)
Brand Name: SAW H10Mn2 welding wire
Model Number: SAW H10Mn2 welding wire
Material:
Length:
Operating Current:
Welding Current:
Operating Temperature:
Diameter:
Application:

Specifications

According with GB H10Mn2             SAW  H10Mn2
Corresponding with AWS EH14
Introduction: It is a kind of high-manganese type welding wire. It matches with low-manganese and low-silicon type welding flux. It is not sensitive to the rust on the base metal. It has excellent bead molding and slag detachability. Monopole or dipole. AC/DC.
Uses: Used together with fused flux 350 or sintered flux 101. Used for both high speed welding and filling welding on 50kg class base metals. The deposited metal has very stable mechanical properties.

Chemical Composition of Welding Wire(%)

C

Mn

Si

S

P

Ni

Cr

 0.12

1.5~1.9

 0.07

 0.035

 0.035

 0.30

 0.20

Mechanical Properties of Deposited Metal

Test Items

 

b

 s

5

AKV(J)

Flux Used Together

 

(MPa)

(MPa)

(%)

-20℃

301

490-650

 400

 22

 34

350

415-550

 330

 22

 27

Wire Size

diameter(mm)

 

 2.5

 3.2

 4.0

 5.0

 

 

 

 

 

 

 

SAW EM12