Toughened Glass strength is common glass 3 to 5 times, Toughened glass according to production methods can be divided into chemical toughened and physical toughened method two kinds. Physical toughened method is a method widely used at home and abroad. It is a common plate glass after processing and become a kind of pre-stressed glass again.Toughened glass is near will float glass heated to softening temperature after rapid cooling uniformity, so that the glass surface compressive stress of glass. In the process of cooling, toughened glass outside due to rapid cooling and solidifying, internal cooling slowly, when the internal cooling contraction continues to make the glass surface compressive stress, tensile stress is generated, thus improve the glass strength and thermal stability.Toughened glass surface compressive stress is more than 95 mpa, half toughened glass surface compressive stress between 24-69 mpa. Chemical tempered glass definition: chemical tempered glass (also called ion exchange strengthened glass) : through the ionic exchange, the alkaline metal ion of glass surface is placed by other alkaline metal ion in the molten salt, enhancing its mechanical strength. 

Chemical tempered glass product features: 1. The intensity is high, up to 9 to 15 times as strong as the general glass of, destruction resistant pressure up to 600 MPa. 2. The intensity can be adjusted to the request of the customer. 3. The glass surface smooth, no distortion, no spot. 4.There is no explosive problem. 5.Ultra-thin glass, various kinds of abnormal-shaped glass easy to be processed. 6. The broken glass of granular. 7. Chemical tempered after can be cut, coated, sandwiched glue and reprocessing.