| Place of Origin: | China (Mainland) |
|---|---|
| Brand Name: | CYG |
| Model Number: | RSBJ |
| Tensile Strength: | 17 MPa |
| Ultimate Elongation: | 350% min. |
| Low Temperature Flexibility: | No cracking |
| Water Absorption: | 0.5% max. |
Quick Details
Specifications
The RSBJ wraparound heat-shrinkable repair sleeves are made from composite materials. The sleeves with fiber integrated are very stronger than general sleeves in the thickness of sleeves and density of fiber-PE network. They are suitable for repair of all types of pressurized and non-pressurized cable: aerial, buried, ducted, non-filled or jelly filled with polyethylene or metal jackets.
Features:
High split resistance due to fiber reinforced layer
Limitation of split propagation in case of external damage to the sleeve
The moisture-proof aluminum layer between the fiber-reinforced layer and hot melt adhesive make the closure perform superior moisture-proof function
Reliable hot melt seal of splice against humidity
Hot melt adhesive with wide temperature range
Insensitive to sharp flame setting
Range of closures to suit all cable sizes
Few components, fast and easy installation
Specification:
Selection | Supplysize | Diameter after shrunk | Length | Uesd for cable's diameter (mm) |
RSBJ 43/8 | 43 | 8 | 500 / 1000 | 8～30 |
RSBJ 55/12 | 55 | 12 | 500 / 1000 | 15～40 |
RSBJ 75/15 | 75 | 15 | 500 / 1000 | 20～60 |
RSBJ 92/25 | 92 | 25 | 500 / 1000 | 30～80 |
RSBJ 125/30 | 125 | 30 | 500 / 1000 | 40～100 |
RSBJ 160/42 | 160 | 42 | 500 / 1000 | 50～160 |
RSBJ 200/50 | 200 | 50 | 500 / 1000 | 60～200 |
We can design and compound special specified products according to the customers' requirements.
Material Properties | Test Method | Requirement |
Tensile Strength | ISO 37 | 17 MPa |
Ultimate Elongation | ISO 37 | 350% min. |
Density | ISO 1183 Method A | 1.0 – 1.2 g/cm3 |
Hardness | ISO 868 | 50 – 70 D |
Accelerated Ageing | ISO 188 7 days at150°C±2°C | |
Tensile Strength | ISO 37 | 14 MPa min |
Ultimate Elongation | ISO 37 | 300% min. |
Thermal Endurance | IEC 60216 | 120°C |
Low Temperature Flexibility | ASTM D2671 Procedure C 4 hours at –30°C±3°C | No cracking |
Electric Strength | IEC 60243 | 1 mm 180 kV/cm min. 3.5 mm 120 kV/cm min. |
Volume Resistivity | IEC 60093 | 1 x 1012 Ω cm min. |
Dielectric Constant | IEC 60250 | 5 max. |
Water Absorption | ISO 62 Method 1 14 days at23°C±2°C | 0.5% max. |
Resistance to Liquids | ISO 1817 7 days in transformer oil at23°C±2°C(VDE 0370) | No swelling and cracking |
Tensile Strength | ISO 37 | 14 MPa min. |
Ultimate Elongation | ISO 37 | 300% min. |
Resistance to Fungi | ASTM G21 | Pass Rating 1 |
Technical Data