| Place of Origin: | China (Mainland) |
|---|---|
| Brand Name: | Xinda |
| Model Number: | 42CrMo |
| Thickness: | 10~450mm |
| Width: | 50~500mm |
| Length: | 2.5m to 5.5m |
| Application: | tool steel |
| Technology: | Forged |
| Delivery Condition: | hot rolled/forged,annealed/quenched and tempered |
| Surface Condition: | Black Surface,Milled Surface |
| Tolerance for thickness: | -0/+1.0mm(for milled surface),-0/+5.0mm(for black surface) |
| Tolerance for width: | -0/+5.0mm(for milled surface),-0/+10.0mm(for black surface) |
| Hardness: | less than 230HB |
Quick Details
Specifications
|
1.2312 steel flats |
||||||||
| Chemical Composition(%) | ||||||||
| C | Si | Mn | P | S | Cr | Mo | ||
| 0.35-0.45 | 0.20-0.40 | 1.30-1.60 | ≤0.035 | ≤0.035 | 1.80-2.10 | 0.15-0.25 | ||
| Use | ||||||||
|
1. zinc, aluminum, magnesium and other alloy die-casting molds |
||||||||
|
2.heat dies and all kinds of hot forged molds |
||||||||
|
3. Metal extrusion die holder |
||||||||
| Heat Treatment | ||||||||
| 1. preheating 2-4 hours in 500-600°C | ||||||||
| 2. keeping temperature for 2 hours in 850-880°C | ||||||||
| 3. oil cooling to reach 50-100°C | ||||||||
| 4. after quenching can reach a hardness of 50-52HRC, then tempered at 200°C, then hardness can reach above 48 HRC. | ||||||||
| Melting Process | ||||||||
| 1. EAF: Electric Furnace+LF+VD(Optional) | ||||||||
| 2. ESR: Electric Furnace+LF+VD+Eleroslag Remelted(Optional) | ||||||||
| UT Class | ||||||||
| According to Standard of SEP 1921/84,100% Volume, Level C/c, D/d or E/e | ||||||||
| Tolerance on Quantity | ||||||||
| +/-10% Per Size | ||||||||