CHLORINATED POLYETHYLENE ELASTOMER(CM)
CM3675 is applied for wires,and cables and rubber hoses industries,its mechanical property is good,the appearance of the finished products is bright and clean and obtains very good processing property.
Chlorine content (%) | 35±1 |
Heat of fusion (J/g) (≤) | 1.5 |
Shore hardness (A ≤) | 55 |
Tensile strength (Mpa ≥) | 6.0 |
Elongation rate(% ≥) | 700 |
Money viscosity ML(1+4) 125℃ | 70~80 |
Residue on sieve (0.8mm) % ≤ | — |
The number of colored particles (unit/200g ≤) |
|
Stable time (165℃)min ≥ ) |
|
Surface density (g/mL ) ≥ | — |
Melt index (190℃,21.6kg) ≥ | — |
Ash content (%) ≤ | 4.5 |
CPE135A
CPE135A is plastics modification product, it obtains good anti-caking and rapid plasticizing properties, softness property under low temperature, and good mechanical property. It is widely used for PVC modification, ACR and MBS modification, magnetic materials, films, weatherstrip, waterproof roll, etc.
Chlorine content (%) | 35±1 |
Heat of fusion (J/g) (≤) | 1.5 |
Shore hardness (A ≤) | 60 |
Tensile strength (Mpa ≥) | 6.0 |
Elongation rate(% ≥) | 600 |
Money viscosity ML(1+4) 125℃ | 65~85 |
Residue on sieve (0.8mm) % ≤ | — |
The number of colored particles (unit/200g ≤) | 40 |
Stable time (165℃)min ≥ ) | 8 |
Surface density (g/mL ) ≥ | — |
Melt index (190℃,21.6kg) ≥ | — |
Ash content (%) ≤ | 4.5 |
CM3665
CM3665 possesses moderate molecular weight, money viscosity and good mechanical property and processing property. It is suitably used in wires and cables, hoses, etc., obtaining good appearance and comparatively high extruding speed.
Chlorine content (%) | 35±1 |
Heat of fusion (J/g) (≤) | 2.0 |
Shore hardness (A ≤) | 65 |
Tensile strength (Mpa ≥) | 8.0 |
Elongation rate(% ≥) | 600 |
Money viscosity ML(1+4) 125℃ | 60~70 |
Residue on sieve (0.8mm) % ≤ | — |
The number of colored particles (unit/200g ≤) | 40 |
Stable time (165℃)min ≥ ) | 8 |
Surface density (g/mL ) ≥ | — |
Melt index (190℃,21.6kg) ≥ | — |
Ash content (%) ≤ | 4.5 |
CM3645
CM3645 is a kind low molecular weight and low money viscosity product, it is easy for processing, and obtains good adhesive strength with other materials surface.
Chlorine content (%) | 35±1 |
Heat of fusion (J/g) (≤) | 1.5 |
Shore hardness (A ≤) | 60 |
Tensile strength (Mpa ≥) | 6.0 |
Elongation rate(% ≥) | 600 |
Money viscosity ML(1+4) 125℃ | 40~50 |
Residue on sieve (0.8mm) % ≤ | — |
The number of colored particles (unit/200g ≤) | 40 |
Stable time (165℃)min ≥ ) | 8 |
Surface density (g/mL ) ≥ | — |
Melt index (190℃,21.6kg) ≥ | — |
Ash content (%) ≤ | 4.5 |
CM3655
CM3655 is suitable for thincables and the products that require comparatively not high mechanical property .Its Mooney viscosity is low, so its mechanical property is not high, but it is very easy for processing.
Chlorine content (%) | 35±1 |
Heat of fusion (J/g) (≤) | 1.5 |
Shore hardness (A ≤) | 55±5 |
Tensile strength (Mpa ≥) | 6.0 |
Elongation rate(% ≥) | 700 |
Money viscosity ML(1+4) 125℃ | 55~60 |
Residue on sieve (0.8mm) % ≤ | — |
The number of colored particles (unit/200g ≤) |
|
Stable time (165℃)min ≥ ) |
|
Surface density (g/mL ) ≥ | — |
Melt index (190℃,21.6kg) ≥ | — |
Ash content (%) ≤ | 4.5 |
CPE135C
CPE135C is applied for flame retardant ABS products,it obtains good melt fluidity ,and it can improve the flame resistance capacity and impact modification capacity.
Chlorine content (%) | 35±1 |
Heat of fusion (J/g) (≤) | 20±4 |
Shore hardness (A ≤) | 75 |
Tensile strength (Mpa ≥) | 6.0 |
Elongation rate(% ≥) | 700 |
Money viscosity ML(1+4) 125℃ | 50~60 |
Residue on sieve (0.8mm) % ≤ | — |
The number of colored particles (unit/200g ≤) |
|
Stable time (165℃)min ≥ ) | 8 |
Surface density (g/mL ) ≥ | — |
Melt index (190℃,21.6kg) ≥ | — |
Ash content (%) ≤ | 4.5 |