yh501, Typical Properties:

Structure: Radial

Styrene content 30%(Weight)

Tensile strength: 20Mpa

Stress at 300%:4.0Mpa

Elongation:500%

Hardness shore(A): 75

solutioh viscosity(10%,25℃,Mpa):500mpa.s

Appearance: white powder

Main application SEBS YH-501:

YH-501 for low molecular weight linear SEBS, with good fluidity and melting characteristics of low viscosity can be used to produce hot-melt (pressure sensitive) Rubber and Plastic Modification and so on.
YH-501 produced using hot-melt pressure-sensitive adhesive tack, peel strength is moderate, good cohesion, and can be used to produce packaging to protect film; in YH-501 by adding an appropriate amount of SIS, can effectively increase their hot-melt pressure-sensitive tack adhesive strength and peel strength, can be prepared by high-performance pressure-sensitive adhesive. YH-501 has a flow of hot melt adhesives produced good performance, good creep resistance, anti-aging characteristics of high cohesive strength can be used to produce high-grade carpet, anti-slip mats on the back of glue; can also be used for wood production , paper, fabric, leather, metal, plastic, etc. The hot melt adhesive.
YH-501 can be used for PP, PS, LDPE, HDPE, PPO, etc. toughening modification, can significantly improve the low-temperature brittleness, for the modification of PP, it can keep the material transparency. The amount of modified plastics is usually 5-20%.