| Place of Origin: | China (Mainland) |
|---|---|
| Brand Name: | Shuangma |
| Model Number: | ER5183 |
| Application: | |
| Material: | Aluminium alloy |
| Wire Gauge: | 1meter |
| Mesh Size: | 0.8-1.6mm for MIG; 2.0-6.0mm for TIG |
| Hole Shape: | Round |
| Surface Treatment: | |
| Technique: | Welded |
| Typical composition in% Si: | 0.4 |
| Typical composition in% Fe: | 0.4 |
| Typical composition in% Cu: | 0.1 |
| Typical composition in% Mn: | 0.05-1.00 |
| Typical composition in% Mg: | 4.30-5.20 |
| Typical composition in% Cr: | 0.05-0.25 |
| Typical composition in% Zn: | 0.25 |
| Typical composition in% Be: | 0.0003 |
| Typical composition in% Ti: | 0.15 |
| Others: | 0.05 |
| Others Total: | 0.15 |
| Yield strength Rp0.2 (Mpa): | 125 |
| Tensile Strength RM (Mpa): | 275 |
| Elongation A5 (Lo=5do) (%): | 17 |
| Test Temperature: | 20 |
Quick Details
Specifications
SAL5183 is with nearly 5% magnesium and some of manganese. And this product is of high toughness, good forgeability, and well anti-corrosiveness, Furthermore, this is a good choice for color-match in welding after anodic process.But for some alloy, the strength of welding joint is a little higher than 5356.
The model 5183 do not suggested to use in aluminum alloy workpiece which working temperature is over 65℃,thus will cause corrosion cracking in welded joints. You should strictly clean the oxide film on the edge of the workpiece and oil before welding, otherwise it will make bad weld produce and cause porosity, slag inclusion and other defects. Also you can use a plate to hold molten metal to ensure meld form.
The strength of ER5183 is higher than ER5356, which used in high strength situation, especially for crack after welding with other brand or other type aluminum welding wires. SAL5183 is with nearly 5% magnesium and some of manganese. And this product is of high toughness, good forgeability, and well anti-corrosiveness, Furthermore, this is a good choice for color-match in welding after anodic process.
Usage: The argon arc welding of Aluminum & Magnesium alloy welding wires is used as the filler material, used in pressure vessel of chemical industry, nuclear industry, ship-building, boiler, space industry, etc.
aluminum alloy welding wire
er4043,5183,4047,1100
Diameter: 0.8-5.0mm
spool or box packing
ISO9001:2008,SGS
Aluminium Alloy Welding Wire ER4043, ER5356, ER5183 and ER1100
Product Description
Aluminum welding wire,rich specification.
ER 5356&4043 are most popular type.
Wire dia.: 0.8mm 0.9mm 1.0mm 1.2mm 1.6mm 2.0 2.4mm
Tig Rod:1.6 mm 2.0mm 2.4mm 3.2mm 4.0mm 5.0mm 6.0mm
Packing: 0.5kg 2kg,5kg,6-7kg
Certification: ISO 9001:2008 and SGS
Main market: Saudi Arabia, Russia, Berlarus,Brazil etc.
|
Code |
Chemical composition(%) |
|||||||
|
Si |
Fe |
Cu |
Mn |
Mg |
Cr |
Zn |
Ti |
|
|
ER1060 |
0.25 |
0.35 |
0.05 |
0.03 |
0.03 |
---- |
0.05 |
0.03 |
|
ER1100 |
0.95 |
0.95 |
0.05-0.20 |
0.05 |
---- |
---- |
0.10 |
---- |
|
ER4043 |
4.5-6.0 |
0.80 |
0.30 |
0.05 |
0.05 |
---- |
0.10 |
0.20 |
|
ER4047 |
11.0-13.0 |
0.80 |
0.30 |
0.15 |
0.10 |
---- |
0.20 |
---- |
|
ER5356 |
0.25 |
0.40 |
0.10 |
0.05-0.20 |
4.5-5.5 |
0.05-0.20 |
0.10 |
0.06-0.20 |
|
ER5183 |
0.40 |
0.40 |
0.10 |
0.5-1.0 |
4.3-5.2 |
0.05-0.25 |
0.25 |
0.15 |
|
ER5556 |
0.1 |
0.3 |
0.05 |
0.55-8.0 |
4.7-5.2 |
0.05-0.10 |
0.09 |
0.05-0.10 |
Appliacation: Used in bicycles, aluminum scooters and other sports equipment, locomotive car, armory processing, chemical pressure vessel, shipbuilding, aviation and other industries related to aluminum alloy welding.
Advantage:
1. Research melting development and production independently, and chemical component could vary according to different demands
2. use special machine to peel, which decreases air pollution, and avoids pore when welting.
3. Small splash, low noise, easy to form and high efficiency, to prompt melting quality.
4.The surface of metal wire is with high fineness, bright and smooth, has stronger wire feed performance.
5.Arc stability, the perfect outlook of melting ensure production speed and efficiency, which is widely used in many key projects both at home and abroad.
Chemical Component Standard: GB/T3190-1998
Melting wires Standard: GB10858-2008 same with ANSI/AWS A5.10-92
Passed ISO9001:2008 Quality Management System
Package: shrinkable film seal, plus carton and packing belt
Supply mode; Tig Rod(1,000 mm,10kg/carton) and MIG wires(7kg/set)
| Place of Origin: |
Shanxi, China (Mainland)
|
Brand Name: |
Shuangma
|
Model Number: |
Aluminium Alloy Welding Wire ER4043, ER5356, ER5183 and ER1100
|
| Material: |
Aluminum / Aluminum Alloy
|
Diameter: |
0.8-5.0MM,MIG: 0.8, 0.9, 1.0, 1.2, 1.6mm TIG: 1.6, 2.0, 2.4, 3.0, 4.0, 5.0mm
|
Melting Point: |
standard
|
| Weight: |
0.5kg,2kg,6-7kg/spool,or 10kg/box
|
Application: |
used in jointing and overlay processing in the same grade
|
Flux Content: |
standard
|
| Product name: |
aluminum alloy welding wire
|
Standard: |
AWS A 5.10
|
Model: |
er1100, er4043, er4047, er5356, er5183
|
| Type: |
Mig welding wire, Tig welding wire
|
Packing: |
MIG: 0.5kg,2kg,6-7kg/spool; TIG: 5kg, 10kgs/box
|
Feature: |
high quality adopted in various industries
|
| Certification: |
ISO 9001:2008 and SGS
|
Other type welding wire 1: |
ss welding wire
|
Other type welding wire 2: |
flux cored welding wire
|