| Brand Name: | YCMetal |
|---|---|
| Alloy Or Not: | Non-alloy |
| Application: | Construction |
| Type: | Drawn Wire |
| Standard: | AISI |
| Model Number: | 12 |
| Special Use: | Cold Heading Steel |
| Place of Origin: | China (Mainland) |
| Wire Gauge: | 0.7mm-4.0mm |
| Steel Grade: | q195 |
| Material: | q195 low carbon steel wire |
| Surface Treatment: | Black annealed |
| Technique: | annealed and oiled |
| standard weight: | 25-100kg/roll |
| Tensile Strength: | 350-550N/mm2 |
| Wire Diameter: | 8cage to 22cage(4.0mm-0.7mm) |
| feature: | Supersonic cleaning, Hcl cleaning- excellent cleaning. |
| High capacity: | over 1500tons/month for this product |
| Processed: | coil wire, spool wire or big package wire |
| packing: | Plastic inside hessian woven outside or plastic inside nylon woven outside |
Quick Details
Specifications
Black annealed wire
Material Q195
Galvanized wire and all other wire mesh are manufactured by wire rod. Wanlida buy this material from SHANXI ZHONGYANG IRON
and STEEL CO., LTD, which is the biggest steel factory in China. the type of wire rod is Q195, element composition is as follows:
C≤0.07; S≤0.023; Si≤0.09; Mn≤0.32; P≤0.025.Because this type of wire rod has less Impurities, Q195 is fit for drawing.
the diameter is 6.5mm. Generally, Daily output of Wanlida is 120 tons.(electro and hot-dipped are separately 60 tons)
Drawing
Galvanized wire's first stage is drawing.
There are two kinds of drawing machine: powder drawing and water drawing. Powder drawing is fit for junior drawing(6.5mm~4.0mm).
One powder drawing machine has 4 tanks and 4 molds. One tank is matched with a mold. Each of them are offered energy by a electromotor.
0.9mm(max)can be "eat" when the wire cross a mold. There are no loss of weight during drawing.
Annealing
Galvanized wire's second stage is anneal.
Anneal is to low the tensile strength of wire. the stove is solid and built with red bricks. the architecture of anneal stove is cuboid.
Different thickness of wire require different temperature. Range is from 700°C to 900°C. Output of the anneal stove, the tensile strength is 400N~600N.
Chlorhydric acid washing
Galvanized wire's third stage is chlorhydric acid washing.
after the draw and anneal, the wire is thinner, softer but also much more dirty. It needs chlorhydric acid washing to remove the impurities.
Chlorhydric acid washing requires water pool and chlorhydric acid pool. the density of chlorhydric acid is 17%. In the Chlorhydric acid pool,
There is a caldron used for the emission of vapor.]