Performance of balls. 

high hardness 
low breakage 
low wear rate 
good wear resistance...

 

1.      physical characteristics:

-          Hardness (HRC): 56-62  (reducing abrasion according to the national standard 56-58 degree high-Cr casting ball)

-          AK(J/cm2): ≥3.0

-          Time of falling balls: ≥13000

-          Microstructure: M+C  (M-Martensite, C-Carbide)

-  

         

2.      Chemical analysis:

C	Si	Mn	Cr	S	P	Mo	Cu	Ni
2.0-3.2	0.3-1.2	1.3-2.2	11-13	≤0.10	≤0.10	0-2.0	0-1.0	0-1.5
2.0-3.0	0.3-1.2	1.3-2.6	15-18	≤0.10	≤0.10	0-2.0	0-1.0	0-1.5
2.0-2.8	0.3-1.0	1.3-2.6	18-22	≤0.08	≤0.10	0-2.5	0-1.0	0-1.5
2.0-2.8	0.3-1.0	1.3-2.6	22-28	≤0.08	≤0.10	0-3.0	0-2.0	0-1.5

Noted: any need to adjust chemical composition or add alloyed elements, the price would be agreed according to the contract. Chemical composition departure according to GB222-84.

3.      Application fields:

Metal Mines; Cement plants; Power stations; Chemical engineering; Ceramic coating;

4.      Key Benefits:

-          Steady milling conditions due to lower wear rate

-          Constant hardness of all grinding media for each alloy

-          Positive influence on downstream process, especially in the case of flotation

-          Lower freight and handling costs thanks to lower consumption

-          Reduce man hours

5.      Specification (mm)

       Φ12.7,Φ15,Φ17,Φ20,Φ25,Φ30,Φ40,Φ50,Φ60,Φ70,Φ80,Φ90-130
6.      Packing:

Ton bags: 1000Kg per bag

Iron drum: 850-920Kg per drum