K415 EM12K welding wires

According with GB H10Mn2             SAW  H10Mn2

Corresponding with AWS EH14

　　　　　　　　Introduction: It is a kind of high-manganese type welding wire. It matches with low-manganese and low-silicon type welding flux. It is not sensitive to the rust on the base metal. It has excellent bead molding and slag detachability. Monopole or dipole. AC/DC.

Uses: Used together with fused flux 350 or sintered flux 101. Used for both high speed welding and filling welding on 50kg class base metals. The deposited metal has very stable mechanical properties.

Zander welding industry.

SHANDONG ZANDER RESOURCING COMPANY LIMITED

K415 Metal Spool Submerged Arc Welding Wire 

K415 EM12K welding wires

K415 EM12 H08MnA welding wires

K415 3.2mm EM12K welding wires

Chemical Composition of Welding Wire(%)

C	Mn	Si	S	P	Ni	Cr
0.12	1.5~1.9	0.07	0.035	0.035	0.30	0.20

Mechanical Properties of Deposited Metal

Test Items	b	s	5	AKV(J)
Flux Used Together	(MPa)	(MPa)	(%)	-20℃
301	490-650	400	22	34
350	415-550	330	22	27

Wire Size

diameter(mm)

2.5

3.2

4.0

5.0