| Brand Name: | Huayi |
|---|---|
| Model Number: | MT-12A |
| Refractoriness (Degree): | Common (1580°< Refractoriness< 1770°) |
| MgO Content (%): | 78 |
| Material: | MgO-Carbon Brick |
| Shape: | Brick |
| Place of Origin: | China (Mainland) |
| name: | Magnesia Carbon Brick |
| delivery time: | 15 days |
| bulk density: | 2.98 |
Quick Details
Specifications
Magnesia carbon
brick series used for the electric furnace are made by adoption of fused
magnetite, high-purity magnesium sand and graphite as principal raw material,
through high-pressure molding and low-temperature treatment. This product is
mainly used for electric furnace lining, which enjoys advantages including high
temperature resistance strength, corrosion and spalling resistance. According
to the smelting conditions and the kind of smelting steel, different brands
magnesia carbon bricks are available
Physical and chemical indexes (1)
|
Brand |
MT-12A |
MT-12B |
MT-12C |
MT-14A |
MT-14B |
MT-14C |
|
|
Chemical Composition/%,≥ |
MgO |
78 |
76 |
74 |
76 |
74 |
72 |
|
C |
12 |
12 |
12 |
14 |
14 |
14 |
|
|
Apparent porosity/%,≤ |
4 |
5 |
6 |
4 |
5 |
6 |
|
|
Bulk density,≥ g/cm3 |
2.98 |
2.96 |
2.95 |
2.98 |
2.96 |
2.95 |
|
|
Crushing strength,≥ /Mpa |
40 |
40 |
35 |
40 |
40 |
35 |
|
|
Hot modulus of rupture,≥ (1450℃) /Mpa |
8 |
7 |
6 |
12 |
10 |
8 |
|
Physical and chemical indexes (2)
|
Brand |
MT-16A |
MT-16B |
MT-16C |
MT-18A |
MT-18B |
MT-18C |
|
|
Chemical Composition/%,≥ |
MgO |
74 |
72 |
72 |
72 |
70 |
70 |
|
C |
16 |
16 |
16 |
18 |
18 |
18 |
|
|
Apparent porosity/%,≤ |
4 |
5 |
5 |
3 |
4 |
5 |
|
|
Bulk density,≥ g/cm3 |
2.93 |
2.90 |
2.90 |
2.90 |
2.88 |
2.85 |
|
|
Crushing strength,≥ Mpa |
40 |
35 |
30 |
40 |
35 |
30 |
|
|
Hot modulus of rupture,≥ (1450℃) /Mpa |
11 |
8 |
5 |
10 |
7 |
4 |
|