| Model Number: | PT |
|---|---|
| Brand Name: | YIMEI |
| Place of Origin: | China (Mainland) |
| Transparency: | Transparent |
| Processing Type: | Multiple Extrusion |
| Hardness: | Soft |
| Feature: | Moisture Proof |
| Usage: | Packaging Film |
| Type: | Stretch Film |
| Material: | BOPP |
Quick Details
Specifications
Type: PT
Application: Used for paper composite, with good performance of light extinction, the package appears elegant. After composite, it can be used for the composite bag producing with PE or CPP; composite with nonwoven fabric to producing many kinds of hand bags.
Characteristic: * Low static property * High Haze & Matt of uniform
* Excellent printability * Excellent fine ink adhesion
* Excellent Dimensional Stability * High tensile strength
Corona Treatment: Single Side
Typical Thickness: 15μm, 18μm, 20μm
Technical Index:
|
Testing methods |
Unit |
Standard value |
Typical values |
||
|
Physical |
|||||
|
Coefficient of friction |
GB/T10006-1988 |
- |
≤0.8 |
0.34 |
|
|
Gloss 45° |
GB8807-1988 |
- |
≤15 |
10.2 |
|
|
Haze |
GB2410-2008 |
% |
≥70 |
79.3 |
|
|
Mechanical |
|||||
|
Tensile Strength |
MD |
GB/T1040.3-2006 |
MPa |
≥120 |
148 |
|
TD |
≥200 |
245 |
|||
|
Elongation |
MD |
GB/T1040.3-2006 |
% |
≤200 |
150 |
|
TD |
≤70 |
50 |
|||
|
Secant modulus |
MD |
GB/T1040.3-2006 |
MPa |
≥1200 |
1400 |
|
TD |
≥1500 |
2000 |
|||
|
Barrier |
|||||
|
Water vapor permeability |
GB/T1037-1988 |
g/(m2 ·24h·0.1mm) |
≤2.0 |
1.0 |
|
|
Dimensional Stability |
|||||
|
Thermal Shrinkage |
MD |
GB/T10003-2008 120 oC, 2min |
% |
≤4.0 |
3.0 |
|
TD |
≤3.0 |
1.0 |
|||
|
Others |
|||||
|
Wetting tension |
GB/T14216-2008 |
mN/m |
≥38 |
38 |
|