Submerged Arc Welding Wires (H08A / AWS EL12)

Product Description

Confirm with:

GB/T 5293 F4A2-H08A

AWS A5.17 F60-EL8

BS EN 756-S 35 2 CS S1

ISO 14171-A-S35 2 CS S1

ISO 14171-B-S43A2 CS SU11

Product Discription:

KH-H08A is a submerged arc welding wire of coppersurfaced carbon structural steel, Be used together with fused flux KJ301, KJ301 is silico-calcium neutral agglomerated flux, alkalinity is approx 1.0, It appears a ball granule of gray color about 10~60 mesh in size. They are used together, the arc is stable, slag is easy to remove and bead appearance is excellent. The weld metal is possessed of good mechanical properties.

 Model No.: KH-H08A

Flux contanining: containing flux

Diameter: Φ3.2mm, Φ4.0 mm

Type: Rolling wire

Weight: 25kg, 50kg etc.

Export Markets: Gloal

 Application:

Suitable for carbon-steel(such as Q235,Q195 etc.) and low alloy steel(09Mn2,16Mn,16MnCu etc.).

Chemical composition of wires (%):

	C	Mn	Si	S	P	Cu
Welding wires	0.070	0.4	0.018	0.011	0.014	0.10
Deposited metals	0.058	0.86	0.580	0.015	0.024	0.06

 
Typical mechanical properties of deposited metal :

	Tensile Strength Rm(MPa)	Yield Strength ReL(MPa)	Elongation (%)	AKV Impact value (J)(-20°C)
Standard values	415~550	≥330	≥22	≥27
Sample values	470	365	30	60