410S stainless steel is a low carbon modification of Type 410 stainless steel. Low carbon and optionally a small addition of titanium and/ or columbium minimize austenite formation at high temperatures, thereby restricting the alloy's ability to harden. The material remains soft and ductile even when the material is rapidly cooled from above the critical temperature. This low hardening characteristic helps to prevent cracking when the steel is welded or exposed to high temperatures. The alloy is completely ferritic in the annealed condition. 410S is ferromagnetic. 410F2 is lead free cutting steel,which is not lowered the corrosion resistance of 410 steel. 410J1 is high strength steel grade to further improve the corrosion resistance of 410 steel.410J1 is used for turbine blades and the high temperature parts.

1.410S stainless steel chemical composition %:

C(max):0.08, Mn(max):1.00, P(max):0.040, S(max):0.030, Si(max):1.00, Cr:11.5-13.5, Ni:0.60

2.410S stainless steel mechanical properties:

Tensile strength(min):415Mpa, Yield strength(min):205Mpa, Elongation in 2 in. or 50 mm,min, %: 22, Hardness: HB(max): 183, HRB(max):89, Cold bend: 180

3.Payment : Usually 30% of the amount by T/T as deposit , and the balance money shall be paid by T/T after got the faxed B/L.Or L/C at sight .

4.Package: Kraft paper+Hard board+metal/wooden pallet+metal strip; or based on the customer requirement.

5.410S stainless steel application: Tower packing, Distillation trays, Automotive exhaust components, Quenching racks

Henan bebon international Co., Ltd is a professional 410S stainless steel supplier. We can provide the high quality 410S stainless steel plate, 410S stainless steel pipe, 410S stainless steel coil, 410S square/rectangle hollow section with the most competitive price for you. If you want to know 410S stainless steel price, please contact with us!