Product Main

Specifications

Material

Sphere diameter(mm)

HRC

 Broken rate

Impact value

Falling ball numbers

Micro structure

45#

20mm-150mm

≥45

≤1%

≥12J/CM^2

≥10000

 M+C

50Mn

20mm-150mm

45-50 

≤1%

≥15J/CM^2

≥12000

 M+C

60Mn

20mm-150mm

55-60

≤1%

≥15J/CM^2

≥12000

 M+C

65Mn

20mm-150mm

60-65

≤1%

≥12J/CM^2

≥10000

 M+C

B-1

20mm-150mm

50-55

≤1%

≥15J/CM^2

≥12000

 M+C

B-2

20mm-150mm

58-65

≤1%

≥15J/CM^2

≥12000

 M+C

B-3

20mm-150mm

60-65

≤1%

≥15J/CM^2 

≥12000

 M+C

40Cr 

20mm-150mm

45-50 

≤1%

≥12J/CM^2

≥8000

 M+C

 

Chemical Components

 

Material

C

Si

Mn

Cr

Cu

Mo

P

S

45#

0.42-0.50

0.17-0.37

0.5-0.8

0-0.25

0-0.25

0-0.30

0-0.035

0-0.035

50Mn

0.48-0.56

0.17-0.37

0.70-1.0

0-0.25

0-0.25

0-0.30

0-0.035

0-0.035

60Mn

0.57-0.65

0.17-0.37

0.7-1.0

0-0.25

0-0.25

0-0.30

0-0.035

0-0.035

65Mn

0.62-0.70

0.17-0.37

0.9-1.0

0-0.25

0-0.25

0-0.30

0-0.035

0-0.035

B-1

0.52-0.65

0.17-0.37

0.6-1.2

0.25max

 

 

0-0.035

0-0.035

B-2

0.5-0.8

0.17-0.37

0.6-0.8

0.9-1.1

 

 

0-0.035

0-0.035

B-3

0.72-0.92

0.17-0.37

0.7-1.0

0.5-0.9

 

 

0-0.035

0-0.035

40Cr 

0.37-0.45

0.17-0.37

0.5-0.8

0.8-1.1

 

 

 

 

 

Surface treatment: water quenching oil quenching air quenching

 

Feature:

1) In general, forged steel ball has high hardness: surface hardness to 45-65 HRC

2) Impact toughness high: impact toughness more than 12 -15J / cm2. 

3) Broken rate is low: the actual broken rate is not higher than 1%. 

4) Loss of grinding forged steel ball round rate is low. 

 

 

Industries:

Widely used in metallurgical mines, cement, building materials, thermal power, flue gas desulfurization, magnetic materials, chemical industry, coal water slurry, pellets, slag, ultrafine powder, fly ash, calcium carbonate, quartz sand industry such as ball mill.