Wear Blocks combine is a combination of high chromium white iron metallurgical bonded to a mild steel backing plate. The white
iron has a minimum hardness of 700 Brinell (63 Rc) providing maximum abrasion resistance protection for your equipment. The mild
steel is easily weldable with minimal preparation and acts as a cushion for the white iron, enabling it to handle impact and abrasion
in the most extreme applications. Lamination of chrome moly white iron metallurgically bonded to a mild steel backing plate
achieving a high strength joint. Its bonding shear strength is over 30,500 psi (or 210 Mpa) and will not separate.
Wear Blocks combine has established a reputation as the solution for impact and high abrasion in the mining and quarry industries,
and has numerous applications in the sugar cane, recycling, cement, mineral processing and dredging industries among others. Custom Wear Blocks combine parts can be designed to user's specifications.White iron: modified AS2027 20/3 Cr Mo with finished minimum hardness of 700 HB (63 Rc) and
containing primary carbides up to 1500HV.
For coal-crushing and sugarcane shredding, try HardTips. They're easy to install via bolts or welding. Their edges can be rotated to
optimize tip life and overall performance.
Cost effective as compared to hard facing. Superior edge retention and sharpness.
No need to rebuild edges. Increased production and cutting efficiency. Easy to install and maintain.
Ideal for a vast number of wear-prone areas. Available in diameters from 2.25" to 6" and easy to apply, they offer superior protection campared to hand hardfacing or steel strips cut from full sheets of metal wear plates.
Our products are perfectly suited for those localized trouble spots on heavy earthmoving equipment such as buckets, transfer points, and ground-engaging tools.
Ideal for smaller areas requiring wear resistant material.
High-Chromium Moly White Iron: HB700
The material composition:
C: 3.20 - 3.60 Si: 0.40 - 0.90
Mn: 1.40 - 2.00 Cr: 18.00 - 23.00
Ni: ≤2.5 Mo:1.40 - 2.00
Cu: 0.50 - 1.20 V, Ti: ≤0.1
P, S: ≤0.05
| Wear Donuts | Type | A | B | C | D | E | High-Chromium | Tungsten Carbide | |||||||
| mm | in | mm | in | mm | in | mm | in | mm | in | kg | lb | kg | lb | ||
| DLP 1920 | 75 | 75.00 | 3 | 25.00 | 1 | 17.00 | 11/16 | 8.00 | 3/8 | 25.00 | 1 | 0.80 | 1.78 | 1.15 | 2.55 |
| DLP 1921 | 100 | 100.00 | 3 15/16 | 50.00 | 2 | 17.00 | 11/16 | 8.00 | 3/8 | 25.00 | 1 | 1.10 | 2.44 | 1.58 | 3.51 |
| DLP 1994 | 100 | 100.00 | 3 15/16 | 70.00 | 2 13/16 | 24.00 | 1 | 8.00 | 3/8 | 32.00 | 1 5/16 | 1.10 | 2.44 | 1.58 | 3.51 |
| DLP 2196 | 130 | 130.00 | 5 1/8 | 80.00 | 3 3/16 | 15.00 | 5/8 | 8.00 | 3/8 | 23.00 | 1 5/16 | 1.40 | 3.11 | 2.01 | 4.47 |
| DLP 4771 | 148 | 148.00 | 5 13/16 | 108.00 | 4 9/32 | 25.00 | 1.00 | 10.00 | 0.44 | 35.00 | 1 3/8 | 2.20 | 4.89 | 3.16 | 7.02 |