| Classification: | Chemical Auxiliary Agent |
|---|---|
| Brand Name: | HYT |
| Usage: | Electronics Chemicals,Leather Auxiliary Agents,Paper Chemicals,Plastic Auxiliary Agents,Rubber Auxiliary Agents, |
| Type: | Carbon Black |
| Place of Origin: | China (Mainland) |
| Purity: | 90% |
Quick Details
Specifications
| ize | N219 | N220 | N234 | N326 | N330 | N339 | N472 | N539 | N550 | N660 | N774 | N772 |
| lodine Absorption Number g/kg | 118 +/-5 | 121 +/-5 | 120 +/-5 | 82 +/-5 | 82 +/-5 | 90 +/-5 | 250 +/-10 | 43 +/-6 | 43 +/-4 | 36 +/-4 | 29 +/-4 | 30 +/-6 |
| DBP Absorption Number cm 3 /100g | 78 +/-5 | 114 +/-5 | 125 +/-5 | 72 +/-5 | 102 +/-5 | 120 +/-5 | 178 +/-7 | 111 +/-7 | 121 +/-5 | 90 +/-5 | 72 +/-5 | 65 +/-6 |
| DBP Absorption Number of Compressed Sample cm 3 /100g | 68~82 | 93~107 | 93~107 | 62~76 | 81~95 | 94~108 | 107~121 | 77~91 | 81~95 | 68~82 | 52~64 | |
| CTAB Surface Area cm 2 /g | 102~112 | 106~116 | 114~124 | 79~87 | 79~87 | 91~99 | 136~154 | 35~47 | 38~46 | 31~39 | 25~33 | 27~39 |
| Nitrogen Surface Area cm 2 /g | 111~112 | 114~124 | 121~131 | 79~89 | 78~88 | 91~101 | 263~277 | 35~47 | 38~46 | 30~40 | 24~34 | 26~38 |
| Tint Strength % | 118~128 | 110~120 | 119~129 | 107~117 | 98~108 | 105~115 | - | - | - | - | - | - |
| PH Value | - | - | - | - | - | - | - | - | - | - | - | - |
| Heating Loss %≤ | 3.0 | 3.0 | 2.5 | 2.5 | 2.5 | 2.5 | 2.5 | 1.5 | 2.5 | 1.5 | 1.5 | 1.5 |
| Ash Content % | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 |
| No.325 Sieve Residue %≤ | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 |
| No.35 Sieve Residue %≤ | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 | 0.001 |
| No.100 Sieve Residue %≤ | - | - | - | - | - | - | - | - | - | - | - | - |
| Impurity | - | - | - | - | - | - | - | - | - | - | - | - |
| Tensile Strength Mpa≥ | +1.0 | -0.8 | -0.8 | +1.0 | -1.5 | -0.5 | - | -4.5 | -3.5 | -3.5 | -3.5 | - |
| Extension %≥ | +60 | +10 | -10 | +70 | -10 | -30 | - | +60 | -10 | +10 | +20 | - |
| Mpa Modulus at 300% | -6.4 +/-1.3 | -2.5 +/-1.3 | -1.1 +/-1.3 | -5.1 +/-1.3 | -1.7 +/-1.3 | 0 +/-1.3 | -5.0 +/-1.2 | -4.5 +/-1.3 | -1.7 +/-1.3 | -3.5 +/-1.3 | -4.8 +/-1.3 | -5.8 +/- |