| Model Number: | metallized film |
|---|---|
| Brand Name: | CFS/Saifu/SF brand for metallized film |
| Place of Origin: | China (Mainland) |
| Transparency: | Opaque |
| Processing Type: | Multiple Extrusion |
| Hardness: | Soft |
| Feature: | Water Soluble |
| Usage: | Capacitors |
| Type: | Metallized Film |
| Material: | BOPP |
| Usage:: | Capacitor |
| BOPP metallized film: | single,double,center,double-side |
| Elongation at break:: | 40-200%MD |
| BOPP metallized film spraying layer:: | excellent self healing property |
| Density for BOPP metallized:: | 0.905 0.005 |
| Coating square resistance:: | 6-9 heavy edge 2-4 non heavy edge |
| Magin value:: | 2.5mm 2.0mm 1.5mm 1.0mm 0.5mm |
| Model Number:: | metallized film |
| Certificate:: | ISO;SGS;CQC,RoH |
| Processing Type:: | Casting |
Quick Details
Specifications
BOPP film for capacitor water transfer printing film
Products:
Aluminum metallized polypropylene safety film.
Aluminum metalized polypropylene film.
Zinc – Aluminum alloy metallized polypropylene film with heavy edge.
Zinc – Aluminum alloy metallized polypropylene safety film with heavy edge.
Zinc – Aluminum alloy metallized polypropylene film with heavy edge and gradient square resistance.
Aluminum metalized polyester film.
Zinc – Aluminum alloy metallized polyester film with heavy edge.
Packing of Metallized Film :
Roll films are packed in vacuum plastic bag and heat-sealed with desiccants.
Bags are marked with lables of types , thickness, width, free margin width and resistance.
The bags are packed in carton cases.
The cartons are wrapped in wooden cases or reinforced carton.
Storge :
Metallized film should be stored in its original package until its use with temperature 5 ~ 35℃ and humidity less than 85%RH.
Metallized layer is easily oxidized when exposure to moisture. Therefore, the film should be used as soon as possible when opened.
The recommended temperature is 15 -25℃ with humidity less than 60%RH after the package is open.
With original sealed package, and stored in the above mentioned conditions, the storage time can be as following:
Metallized layer is easily oxidized when exposure to moisture. Therefore, the film should be used as soon as possible when opened.
The recommended temperature is 15 -25℃ with humidity less than 60%RH after the package is open.
With original sealed package, and stored in the above mentioned conditions, the storage time can be as following:
Al metalized Film: 12 months from the delivered date..
Al/Zn Alloy metalized Film: As Zn is relatively unstable, preservation period depends on the resistance of the film:
Less than 10 Ohms: 6 months (from delivery date)
10 Ohms to 15 Ohms: 3 months (from delivery date)
Al/Zn Alloy metalized Film: As Zn is relatively unstable, preservation period depends on the resistance of the film:
Less than 10 Ohms: 6 months (from delivery date)
10 Ohms to 15 Ohms: 3 months (from delivery date)
Roll Outer Diameter :
|
Slit widths |
Recommend outer diameter: |
|
4.5mm≤W<10mm |
140mm≤D≤185mm |
|
10mm≤W<25mm |
150mm≤D≤185mm |
|
25mm≤W<50mm |
150mm≤D≤240mm |
|
50mm≤W |
150mm≤D≤350mm |
Specifications of metallized film:
MPP film :
|
Properties |
Unit |
Requirements |
|
|
Density |
g/cm3 |
0.905±0.005 |
|
|
Thickness |
μm |
3.8 ~ 15 |
|
|
tensile Strength |
MD(MPa) |
≥100 |
|
|
Elongation at Break |
MD(%) |
40 ~ 200 |
|
|
Heat Shrinkage |
MD(%) |
≤5 ( 120°C, 10min) ( 120°C , 10 min ) |
|
|
Break-dowm voltage |
V/μm |
≥350 ( 23°C, DC ) |
|
|
Coating square resistance |
Ω |
with (heavy-edge) |
(heavy-edge area):3±1 (non heavy-edge area):7.5 ±2.5 |
|
without heavy-edge |
2~4 |
||
|
Dissipation Factor |
_ |
≤4×10^(-4 )(20℃,1KHz ) |
|
|
RC |
ΩF |
≥5×10^4
|
|
If there is a special demand,please contact us at any time ~
There is no perfect individual, only a perfect team! Team, the greatest Power
welcome to visit us, we are very pleased to be your guide, show you our Factory and our city ~
No business too small ,No problem too big .
We will try our best to obey your thirst !!