2015 hot sale high self healing al zn mpp lamination film for capacitor
Products: 

Aluminum metallized polypropylene safety film. 

Aluminum metalized polypropylene film. 

Zinc – Aluminum alloy metallized polypropylene film with heavy edge. 

Zinc – Aluminum alloy metallized polypropylene safety film with heavy edge. 

Zinc – Aluminum alloy metallized polypropylene film with heavy edge and gradient square resistance. 

Aluminum metalized polyester film. 

Zinc – Aluminum alloy metallized polyester film with heavy edge. 

  

Packing of Metallized Film : 

 Roll films are packed in vacuum plastic bag and heat-sealed with desiccants. 

Bags are marked with lables of types , thickness,  width, free margin width and resistance. 

The bags are packed in carton cases.   

The cartons are wrapped in wooden cases or reinforced carton. 

 

Storge : 

Metallized film should be stored in its original package until its use with temperature  5 ~ 35℃ and humidity less than 85%RH.
Metallized layer is easily oxidized when exposure to moisture. Therefore, the film should be used as soon as possible when opened. 
The recommended temperature is 15 -25℃ with humidity less than 60%RH after the package is open.
With original sealed package, and stored in the above mentioned conditions, the storage time can be as following:  

Al metalized Film: 12 months from the delivered date..
Al/Zn Alloy metalized Film: As Zn is relatively unstable, preservation period depends on the resistance of the film:
Less than 10 Ohms: 6 months (from delivery date)
10 Ohms to 15 Ohms: 3 months (from delivery date) 

Roll Outer Diameter : 

Slit widths	Recommend outer diameter:
4.5mm≤W<10mm	140mm≤D≤185mm
10mm≤W<25mm	150mm≤D≤185mm
25mm≤W<50mm	150mm≤D≤240mm
50mm≤W	150mm≤D≤350mm

 

Specifications of metallized film: 

MPP film : 

Properties	Unit	Requirements
Density	g/cm3	0.905±0.005
Thickness	μm	3.8 ~ 15
tensile Strength	MD(MPa)	≥100
Elongation at Break	MD(%)	40 ~ 200
Heat Shrinkage	MD(%)	≤5 ( 120°C, 10min)  ( 120°C , 10 min )
Break-dowm voltage	V/μm	≥350 ( 23°C, DC )
Coating square resistance	Ω	with (heavy-edge)	(heavy-edge area):3±1  (non heavy-edge area):7.5 ±2.5
		without heavy-edge	2~4
Dissipation Factor	_	≤4×10^(-4 )(20℃,1KHz )
RC	ΩF	≥5×10^4

If there is a special demand,please contact us at any time ~   

There is no perfect individual, only a perfect team! Team, the greatest Power 

Thank you for your precious time to watch our products.  

welcome to visit us, we are very pleased to be your guide, show you our Factory and our city ~ 

No business too small ,No problem too big . 

                                   We will try our best to obey your thirst !!