| Width: | 100-300 |
|---|---|
| Thickness: | 0.1-5.0mm |
| Model Number: | W1 |
| Brand Name: | Shibo |
| Place of Origin: | China (Mainland) |
| Density:: | 19.3g/cm3 |
| Surfance state:: | Polishing |
| Melting point: | 3410 degree |
| Technique:: | Annealing polishing |
| Color:: | Metallic |
| Shape:: | plate |
| Certification: | ISO9001-2000 |
| Grade: | W1 |
| purity: | 99.95% |
| Name: | Hot sale 99.95% pure tungsten sheet metal |
Quick Details
Specifications
0.5mm 99.95% pure Tungsten sheet/plate for sapphire crystal growth
A.Grade: W1,W2,WAL1,WAL2
B. Purity :> =99.95%
C. Characteristic:
.Melting Point: 3410 Degrees Celsius
.Boiling Point: 5927 Degrees Celsius
.Density: 19.3 g/cm3
. Product Feature: High melting point, Highdensity, high temperature oxidation resistance, long service life,
resistance to corrosion.
1.Tungsten Mechanical Properties
|
Tungsten Mechanical Properties |
||
|
Tensile Strength |
KSI (Mpa)-RT |
250 (1725) |
|
|
KSI (Mpa)-500°C |
150 (1035) |
|
|
KSI (Mpa)-1000°C |
75 (515) |
|
Elongation |
% in 1.0". |
-- |
|
Hardness |
DPH |
300 |
|
Modules of Elasticity |
KSI |
58000 |
|
|
Gpa |
400 |
Tungsten plate Specifications
|
Thickness (mm) |
Width (mm) |
Length (mm) |
|
0.05-0.1 |
100 |
500 |
|
0.1-0.15 |
100 |
600 |
|
0.15-0.20 |
205 |
1000 |
|
0.20-0.30 |
300 |
1000 |
|
0.30-0.50 |
350 |
1000 |
|
0.5-8.0 |
400 |
1000 |
|
0.80-1.00 |
330 |
1000 |
|
1.0-1.5 |
400 |
1000 |
|
1.5-3.0 |
300 |
1000 |
|
>3.0 |
300 |
L |
2. Tungsten plate Application
Tungsten has a unique property of which it's melting point can reach 3410 tungsten,
is widely applied in high temperature vacuum furnace melting environment such as
sapphire growing furnace, quartz glass melting furnace, and rare earth melting furnace.
For sapphire crystal growing furnace, high-purity, high-density, no crack,
tungsten crucible with other features of exact measurement and smooth surface
has decisive influence on the success of crystal growth, quality control of pulling crystal, discharging
and service life during sapphire growing.
3. Tungsten composition
|
Impurity Content≤% |
|||||||||
|
Al |
Ca |
Fe |
Mg |
Mo |
Ni |
Si |
C |
N |
O |
|
0.002 |
0.005 |
0.005 |
0.003 |
0.01 |
0.003 |
0.005 |
0.008 |
0.003 |
0.005 |
4. Production engineering
Materials--hot rolling—annealing--cold rolling ---leveling---annealing---machining---tungsten plates