FaRetar^TM Mg(OH)₂  MH-02

Characteristics  

Natural mineral magnesium hydroxide is obtained by screening, grinding and surface modifying of brucite. It has high purity, ideal particle size and is used as flame retardant or anti-smoke agent. 
Specification 

Item	Specification
	A	B	C
Mg(OH)2, %	≥ 95
CaO, %	≤ 1.5
SiO2, %	≤ 2.0
Particie size (D50), μm	≤ 2	≤ 3	≤ 5
Particie size (D97), μm	≤ 7	≤ 10	≤ 20
Water, %	≤ 0.5
Fe3+, %	≤ 0.5
Cl-, %	≤ 0.01
Whiteness, %	≥ 94	≥ 93	≥ 92
Lgnition loss, %	≥ 28.5

Applications
Low-smoke & halogen free wire and cable
Rubber products
Polymer engineering plastics
Paint
Coating
 
Characteristics 
FaRetar^TM Mg(OH)₂ MH-04, which is produced by chemical synthesized method, has the appearance of hexagonal flake with good dispersibility. MH-04 can also be modified by stearic acid, titanate, silane or according to the customer's requirement. MH-04 is widely used in low-smoke & halogen free wire and cable, rubber, construction materials and pharmaceutical area.
Specification 

Item	Specification
Mg(OH)2, %	≥ 99
CaO, %	≤ 0.2
SiO2, %	≤ 0.1
Particie size (D50), μm	≤ 1.5
Particie size (D97), μm	≤ 5
Bulk density, g/mL	≤ 0.3
Whiteness, %	≥ 95
Water, %	≤ 0.3
Fe3+, %	≤ 0.01
Cl-, %	≤ 0.1
Lgnition loss, %	≥ 29
Specific surface area, m2/g	< 8
Sieve residue, %	≤ 0.02

 
Applications
Low smoke non-halogen cable material
Rubber
EVA
PF
EP 
 
Characteristics 
FaRetarTM Mg(OH)₂ MH-06 is produced by MgCl and NaOH. It can be modified by silane, stearic acid, PAEs or according to the customer's requirement. 
 Specification 

Item	Specification
	A	B	C
Mg(OH)2, %	≥ 98.5
CaO, %	≤ 0.1
SiO2, %	≤ 0.01
Particie size (D50), μm	≤ 2	≤ 3	≤ 5
Particie size (D97), μm	≤ 7	≤ 10	≤ 20
Water, %	≤ 0.5
Fe3+, %	≤ 0.005
Cl-, %	≤ 0.07
Whiteness, %	≥ 96
Lgnition loss, %	≥ 29.5

 
Applications
Low smoke non-halogen cable material
Rubber
EVA
Bactericide and water purifying agent 
Biological pharmacy
Food 
Burning high purity magnesium oxide
Packing
20 kg per bag.