Introduction

Ultrafine precipitated FaRetar^TM Al(OH)₃ is regular crystal structure products made by additional process. It has the benefits of high-purity, ultrafine-precipitated, regular crystal shape, low surface activity and small specific surface area, can be widely used in various of processing technology.
FaRetar^TM Al(OH)₃ working principle is absorbing heat and decomposing into alumina and water, without generating toxic gas and corrosive substance, the decomposition process absorbs lots of heat during the polymer's combustion, to prevent polymer rapid decomposition and delaying the formation of flammable by-products. The water vapor produced displaces oxygen to play a similar role of inert gas. A protective layer formed by alumina and carbon products on the surface of the polymer to suppress combustion and lower the smoke density.
Specification

Item	Typical analysis
Al(OH)3, %	≥ 99.4
SiO2, %	≤ 0.02
Na2O, %	≤ 0.3
Fe2O3, %	≤ 0.02
Loss on ignition, %	34.5 ± 0.5
pH	8.0 - 10.0
Electrical conductivity, μs/cm	≤ 150
Moisture, %	≤ 0.3
Whiteness, %	≥ 96
D50, μm	1.3 - 2.1
Oil absorption (linseed oil), mL/100g	≤ 50
Na2O (soluble), %	≤ 0.03
Specific surface area, m2/g	3 - 6
Density, g/cm3	2.4
Refractive index	1.58
Sieve analysis (% on 325 mesh), %	≤ 0.1

 
Application 
FaRetar^TM Al(OH)₃ is the most consumable and applicable inorganic additive flame retardant. It not only resists firing, but also prevents from smoke, dropping or toxic gas. So, it is widely used in the sectors of hot solidifying and moulding plastic, synthetic rubber, coating and construction materials with gradual increase of the usage, at 
Package and Storage
25 kg/bag, Composite paper-plastic bag.
Stored dry and ventilated place.