LHH08MnA
Meeting the Standard of GB H08MnA, Be equivalent to AWS EM12 JIS W21.
Description:
It is middling manganese and middling silicon wire which matches to the high manganese and silicon flux, having the characters of insensitive to the rust on base metal , excellent performance in welding form and deslagging.it is suitable for unipolar and bipolar,also AC and DC welding.
Application:
Description:
It is middling manganese and middling silicon wire which matches to the high manganese and silicon flux, having the characters of insensitive to the rust on base metal , excellent performance in welding form and deslagging.it is suitable for unipolar and bipolar,also AC and DC welding.
Application:
| SAW Wire EM12 | C | Mn | Si | S | P | Cr | Ni | Cu |
| Welding wiresEM12 | 0.066 | 0.88 | 0.022 | 0.013 | 0.010 | 0.020 | 0.021 | 0.075 |
| Deposited metals | 0.046 | 1.14 | 0.180 | 0.014 | 0.018 | 0.040 | 0.011 | 0.070 |
Typical mechanical properties of deposited metal :
| EM12 |
Tensile Strength Rm(MPa) |
Yield Strength ReL(MPa) |
Elongation (%) |
AKV Impact value (J)(-20°C) |
| Standard values | 415~550 | ≥330 | ≥22 | ≥27 |
| Sample Values | 470 | 370 | 30 | 120 |