| Flux Content: | no |
|---|---|
| Application: | welding |
| Weight: | 25kg,100kg,250kg,300kg |
| Diameter: | 2.0-4.0mm |
| Material: | Copper / Copper Alloy |
| Model Number: | EM12 |
| Brand Name: | luhan |
| Place of Origin: | China (Mainland) |
Quick Details
Specifications
Specifications
EM 12 K
1)The weld metal shows a Fine appearance.
2) Both AC and DC can be applied.
3)Stable Arc
4)Easily removable residue
Submerged Arc Welding Wire EM12 K
The products easily removable residue, good seam forming and highly efficient deposiyion. Wire meltingdoes not lead to splash or strong flasing. The sem surface is smooth and welding quality is guaranteed. They facilitate mechanical and automatic welding process. With a wide range of welding parameters, the wires can be used in open fields with strong wind and applied to automobiles, ships, bridges and chemical engineering.
Main Applications:
It is suitable to weld 450Mpa-500Mpa grade structures, such as boilers, ships, bridges, pressure vessels, as well as LPG cylinders, Before welding, the base metal must clear away impurities and fht flux must be baked in a temperature of 300° C-350° C for 1-2 hours.
Typical mechanical properties of deposited metal :
EM 12 K
1)The weld metal shows a Fine appearance.
2) Both AC and DC can be applied.
3)Stable Arc
4)Easily removable residue
Submerged Arc Welding Wire EM12 K
The products easily removable residue, good seam forming and highly efficient deposiyion. Wire meltingdoes not lead to splash or strong flasing. The sem surface is smooth and welding quality is guaranteed. They facilitate mechanical and automatic welding process. With a wide range of welding parameters, the wires can be used in open fields with strong wind and applied to automobiles, ships, bridges and chemical engineering.
Main Applications:
It is suitable to weld 450Mpa-500Mpa grade structures, such as boilers, ships, bridges, pressure vessels, as well as LPG cylinders, Before welding, the base metal must clear away impurities and fht flux must be baked in a temperature of 300° C-350° C for 1-2 hours.
| SAW Wire EM12 | C | Mn | Si | S | P | Cr | Ni | Cu |
| Welding wiresEM12 | 0.066 | 0.88 | 0.022 | 0.013 | 0.010 | 0.020 | 0.021 | 0.075 |
| Deposited metals | 0.046 | 1.14 | 0.180 | 0.014 | 0.018 | 0.040 | 0.011 | 0.070 |
Typical mechanical properties of deposited metal :
| EM12 |
Tensile Strength Rm(MPa) |
Yield Strength ReL(MPa) |
Elongation (%) |
AKV Impact value (J)(-20°C) |
| Standard values | 415~550 | ≥330 | ≥22 | ≥27 |
| Sample Values | 470 | 370 | 30 | 120 |